Influence of temperature on the galvanic current induced by a localized repair when using primers to the reinforcement in slightly chloride contaminated concrete
Abstract An electrochemical macrocell between repaired and adjacent unrepaired zones has been reported when a local concrete patch is performed. This macrocell seems to lead to the corrosion of neighboring not repaired zones. Previous experiments of the authors in slightly chloride contaminated concrete have shown that the macrocell activity lasts very short time (only during the curing). In present paper the effect to rise the temperature to 40°C maintaining the RH, typical of tropical climates, is studied. The results show that the galvanic effect is not enhanced while the corrosion rate does it, which confirms the independence of the galvanic current from the corrosion rate.
Résumé Quand le béton est réparé localement on dit qui une macrocouple entre les zones si et non réparées se forme. Cette macrocouple est dite qu’accélère la corrosion des zones voisines de la part réparée. Dans des articles publiés par les auteurs sur béton avec une quantité modérée des chlorures on a vérifié que l’action galvanique a une très courte durée (seulement pendant le période de cure). Dans la présente étude ce qui a été essayé est l’effet d’une élévation de la température à 40°C en maintenant l’humidité relative. Les résultats montrent que le courant galvanique ne change presque pas mais la vitesse de corrosion augmente, ce que confirme que la corrosion est principalement dû à l’action des microcouples.
Influence of temperature on the galvanic current induced by a localized repair when using primers to the reinforcement in slightly chloride contaminated concrete
Abstract An electrochemical macrocell between repaired and adjacent unrepaired zones has been reported when a local concrete patch is performed. This macrocell seems to lead to the corrosion of neighboring not repaired zones. Previous experiments of the authors in slightly chloride contaminated concrete have shown that the macrocell activity lasts very short time (only during the curing). In present paper the effect to rise the temperature to 40°C maintaining the RH, typical of tropical climates, is studied. The results show that the galvanic effect is not enhanced while the corrosion rate does it, which confirms the independence of the galvanic current from the corrosion rate.
Résumé Quand le béton est réparé localement on dit qui une macrocouple entre les zones si et non réparées se forme. Cette macrocouple est dite qu’accélère la corrosion des zones voisines de la part réparée. Dans des articles publiés par les auteurs sur béton avec une quantité modérée des chlorures on a vérifié que l’action galvanique a une très courte durée (seulement pendant le période de cure). Dans la présente étude ce qui a été essayé est l’effet d’une élévation de la température à 40°C en maintenant l’humidité relative. Les résultats montrent que le courant galvanique ne change presque pas mais la vitesse de corrosion augmente, ce que confirme que la corrosion est principalement dû à l’action des microcouples.
Influence of temperature on the galvanic current induced by a localized repair when using primers to the reinforcement in slightly chloride contaminated concrete
Andrade, C. (author) / Castro, P. (author) / Pazini, E. (author)
Materials and Structures ; 41 ; 351-361
2007-06-01
11 pages
Article (Journal)
Electronic Resource
English
| British Library Online Contents | 2008
Macrocell Activity in Slightly Chloride-Contaminated Concrete Induced by Reinforcement Primers
| British Library Online Contents | 2003