Fibre spacing in steel fibre reinforced composites

Kasperkiewicz, J.

Abstract A method is presented which makes it possible to evaluate the fibre content or to estimate the distribution of fibres in steel fibre reinforced composite materials from the analysis of X-ray pictures. The basic notion in this method is an apparent fibre spacing defined as the average spacing between the intersections of individual fibre projections upon a certain plane and an arbitrary base line drawn on that plane. Such apparent spacing may be estimated analytically, it may also be measured directly on the radiogram. The comparison of analytical and experimental data shows satisfactory agreement.

Résumé On présente une méthode qui, par l'analyse des diagrammes de rayons-X, permet d'évaluer la teneur en fibre ou d'estimer leur distribution dans des composites renforcés de fibres d'acier. On suppose que la distribution des fibres est homogène et isotropique, toutes les fibres ayant même longueur et même diamètre. En tant que notion de base de cette méthode, on définit un espacement de fibres apparent comme l'espacement moyen entre d'une part les intersections des projections des fibres individuelles, et d'autre part une ligne de base arbitraire tracée sur le même plan. Un tel espacement apparent (s app. anl. ) peut être évalué analytiquement comme une fonction de la longueur de la fibre (l), du diamètre (d) de la teneur en volume (β) et de l'épaisseur de l'échantillon (w)-équation (7). On peut aussi le mesurer directement sur le radiogramme commes app. exp. [voirfig. 2, équation 12)]. La comparaison des résultats analytiques et expérimentaux (tableau I) montre une bonne concordance. On peut aussi se servir de la méthode pour évaluer l'épaisseur d'échantillons soumis aux rayons-X, ce qui prouverait une bonne lisibilité du radiogramme.