Effect of supercritical carbonation on porous structure and mechanical strength of cementitious materials modified with bacterial nanocellulose
https://orcid.org/http://orcid.org/0000-0002-6087-3255
The effect of wet supercritical CO2 (90 °C and 20 MPa) on the performance of cement paste (PC) modified with bacterial nanocellulose (BNC) was investigated. The pore structure of carbonated cement shows clogging over the outer rim of the samples. In contrast, near the sample core, the characteristic peak of pore size distribution shifted towards smaller pores analyzed by mercury intrusion porosimetry. The effect of the carbonation over time on mechanical properties shows increasing alteration. XRD results show more crystalline phases of hydrated cement in the BNC samples before carbonation. Cement reinforced with BNC shows lower density, a reduction in its porosity, and experiences fewer porosity changes at the cement core. Furthermore, its mechanical performance was less affected by the carbonation process.
Effect of supercritical carbonation on porous structure and mechanical strength of cementitious materials modified with bacterial nanocellulose
https://orcid.org/http://orcid.org/0000-0002-6087-3255
The effect of wet supercritical CO2 (90 °C and 20 MPa) on the performance of cement paste (PC) modified with bacterial nanocellulose (BNC) was investigated. The pore structure of carbonated cement shows clogging over the outer rim of the samples. In contrast, near the sample core, the characteristic peak of pore size distribution shifted towards smaller pores analyzed by mercury intrusion porosimetry. The effect of the carbonation over time on mechanical properties shows increasing alteration. XRD results show more crystalline phases of hydrated cement in the BNC samples before carbonation. Cement reinforced with BNC shows lower density, a reduction in its porosity, and experiences fewer porosity changes at the cement core. Furthermore, its mechanical performance was less affected by the carbonation process.
Effect of supercritical carbonation on porous structure and mechanical strength of cementitious materials modified with bacterial nanocellulose
https://orcid.org/http://orcid.org/0000-0002-6087-3255
The effect of wet supercritical CO2 (90 °C and 20 MPa) on the performance of cement paste (PC) modified with bacterial nanocellulose (BNC) was investigated. The pore structure of carbonated cement shows clogging over the outer rim of the samples. In contrast, near the sample core, the characteristic peak of pore size distribution shifted towards smaller pores analyzed by mercury intrusion porosimetry. The effect of the carbonation over time on mechanical properties shows increasing alteration. XRD results show more crystalline phases of hydrated cement in the BNC samples before carbonation. Cement reinforced with BNC shows lower density, a reduction in its porosity, and experiences fewer porosity changes at the cement core. Furthermore, its mechanical performance was less affected by the carbonation process.
Effect of supercritical carbonation on porous structure and mechanical strength of cementitious materials modified with bacterial nanocellulose
Mater Struct
Barría, Juan Cruz (author) / Manzanal, Diego (author) / Ghabezloo, Siavash (author) / Pereira, Jean-Michel (author)
2023-12-01
Article (Journal)
Electronic Resource
English
Enforced carbonation of cementitious materials
| Elsevier | 2023
Assessing the Carbonation Behavior of Cementitious Materials
| British Library Online Contents | 2006
Assessing the Carbonation Behavior of Cementitious Materials
| Online Contents | 2006