Microstructure and mechanical properties of TiC/Ti matrix composites and Ti-48Al-2Cr-2Nb alloy joints brazed with Ti-28Ni eutectic filler alloy: Fid-Bau Portal

Fachinformationsdienst BAUdigital

A platform for research: civil engineering, architecture and urbanism

Microstructure and mechanical properties of TiC/Ti matrix composites and Ti-48Al-2Cr-2Nb alloy joints brazed with Ti-28Ni eutectic filler alloy

Dong, Duo / Xu, Haitao / Zhu, Dongdong / Wang, Gang / He, Qing / Lin, Junpin

Ti-48Al-2Cr-2Nb and TiC/Ti matrix composites were successfully joined using Ti-28Ni eutectic filler metal at different brazing temperatures. Microstructure and mechanical properties of the joints were systematically studied. The results showed that the joints all showed integral interfaces and the microstructures of the joints for 980 °C/15 min were detected as Ti-48Al-2Cr-2Nb/α₂-Ti₃Al + τ₃-Al₃NiTi₂/α₂-Ti₃Al/Ti(s,s) + δ-Ti₂Ni + TiC/Ti matrix composites. As brazing temperature increased, continuous Ti₂Ni layer diminish and Ti₂Ni phase became more discrete. However, α₂-Ti₃Al rich layer has thickened which deteriorates the properties of the joints. The highest shear strength achieved 469.5 MPa as the joint brazed at 1010 °C for 15 min. The evolution of microstructures brazed with different temperatures was studied and its relationship with the shear strength was also revealed in details.

Access

Check availability in my library

Order at Subito €

Page navigation

Document information

Export, share and cite

Microstructure and mechanical properties of TiC/Ti matrix composites and Ti-48Al-2Cr-2Nb alloy joints brazed with Ti-28Ni eutectic filler alloy

Dong, Duo / Xu, Haitao / Zhu, Dongdong / Wang, Gang / He, Qing / Lin, Junpin

Ti-48Al-2Cr-2Nb and TiC/Ti matrix composites were successfully joined using Ti-28Ni eutectic filler metal at different brazing temperatures. Microstructure and mechanical properties of the joints were systematically studied. The results showed that the joints all showed integral interfaces and the microstructures of the joints for 980 °C/15 min were detected as Ti-48Al-2Cr-2Nb/α₂-Ti₃Al + τ₃-Al₃NiTi₂/α₂-Ti₃Al/Ti(s,s) + δ-Ti₂Ni + TiC/Ti matrix composites. As brazing temperature increased, continuous Ti₂Ni layer diminish and Ti₂Ni phase became more discrete. However, α₂-Ti₃Al rich layer has thickened which deteriorates the properties of the joints. The highest shear strength achieved 469.5 MPa as the joint brazed at 1010 °C for 15 min. The evolution of microstructures brazed with different temperatures was studied and its relationship with the shear strength was also revealed in details.

Microstructure and mechanical properties of TiC/Ti matrix composites and Ti-48Al-2Cr-2Nb alloy joints brazed with Ti-28Ni eutectic filler alloy

Dong, Duo / Xu, Haitao / Zhu, Dongdong / Wang, Gang / He, Qing / Lin, Junpin

Ti-48Al-2Cr-2Nb and TiC/Ti matrix composites were successfully joined using Ti-28Ni eutectic filler metal at different brazing temperatures. Microstructure and mechanical properties of the joints were systematically studied. The results showed that the joints all showed integral interfaces and the microstructures of the joints for 980 °C/15 min were detected as Ti-48Al-2Cr-2Nb/α₂-Ti₃Al + τ₃-Al₃NiTi₂/α₂-Ti₃Al/Ti(s,s) + δ-Ti₂Ni + TiC/Ti matrix composites. As brazing temperature increased, continuous Ti₂Ni layer diminish and Ti₂Ni phase became more discrete. However, α₂-Ti₃Al rich layer has thickened which deteriorates the properties of the joints. The highest shear strength achieved 469.5 MPa as the joint brazed at 1010 °C for 15 min. The evolution of microstructures brazed with different temperatures was studied and its relationship with the shear strength was also revealed in details.

Access

Check availability in my library

Order at Subito €

Page navigation

Document information

Export, share and cite

Document information

Title:

Microstructure and mechanical properties of TiC/Ti matrix composites and Ti-48Al-2Cr-2Nb alloy joints brazed with Ti-28Ni eutectic filler alloy

Additional title:

Archiv.Civ.Mech.Eng

Contributors:

Dong, Duo (author) / Xu, Haitao (author) / Zhu, Dongdong (author) / Wang, Gang (author) / He, Qing (author) / Lin, Junpin (author)

Published in:

Archives of Civil and Mechanical Engineering ; 19 ; 1259-1267

Publication date:

2019-12-01

Size:

9 pages

ISSN:

DOI:

https://doi.org/10.1016/j.acme.2019.07.005

Type of media:

Article (Journal)

Type of material:

Electronic Resource

Language:

English

Keywords:

TMCs , TiAl alloy , Brazing , Microstructure , Shear strength Engineering , Materials Engineering , Civil Engineering , Mechanical Engineering , Structural Materials

Similar titles

Interfacial microstructure and joining properties of Titanium–Zirconium–Molybdenum alloy joints brazed using Ti–28Ni eutectic brazing alloy

Song, X. G. / Tian, X. / Zhao, H. Y. et al. | British Library Online Contents | 2016

Brazing high Nb containing TiAl alloy using Ti–28Ni eutectic brazing alloy: Interfacial microstructure and joining properties

Si, X.Q. / Zhao, H.Y. / Cao, J. et al. | British Library Online Contents | 2015

Brazing high Nb containing TiAl alloy using Ti–28Ni eutectic brazing alloy: Interfacial microstructure and joining properties

Si, X. Q. / Zhao, H. Y. / Cao, J. et al. | British Library Online Contents | 2015

Effect of holding time on microstructure and mechanical properties of Si3N4/Si3N4 joints brazed with Au58.7Ni36.5V4.8 filler alloy

Sun, Y. / Zhang, J. / Fan, G. H. et al. | British Library Online Contents | 2011

Microstructure and strength of brazed joints of Ti3Al-base alloy with TiZrNiCu filler metal

He, P. / Feng, J. C. / Zhou, H. | British Library Online Contents | 2005