Fire resistance of self-compacting concrete, SCC
Abstract This article outlines laboratory and full-scale studies on fire resistance of SCC. For this purpose 40 pre-stressed columns and 140 cylinders of concrete were subjected to compressive loading at high temperature. The SCC included water-binder ratios, w/b, between 0.40 and 0.70 and large amount limestone powder. Comparison was done with vibrated concrete, VC, with the same w/b. Mix proportions were chosen as regards tunnel concrete (w/b=0.40), prefabricated concrete (w/b=0.55) and concrete for production of dwelling houses (w/b=0.70). The waterpowder ratio, w/p varied between 0.28 and 0.70. The fullscale behaviour showed extensive fire spalling for water-cured concrete at w/p<0.40 and for air-cured concrete at w/p<0.35. One way of avoiding the fire spalling was to introduce polypropylene fibres, PPF, in the mix proportions, which was chosen to be very effective. The laboratory results on small cylinders indicated similar material behaviour of SCC and VC at high temperature when spalling did not occur. The project was performed 1999–2002.
Résumé Cet article traite des études en laboratoire et des essais en grandeur nature sur la résistance au feu du béton autocompactant. Pour cette étude, plus de 40 poutres précontraintes et 140 cylindees ont été soumis à des charges compressives à haute température. Le béton présentait un rapport eau/liant se situant entre 0.40 et 0,70 et contenait une forte proportion de poudre de pierre à chaux. Des comparaisons ont été effectuées avec des bétons vibrés ayant le même rapport eau/liant. Les compositions ont été choisies en fonction du béton destiné à la construction de tunnels (0,40), de celui pour la construction préfabriquée (0,55) et du béton destiné à la production d'immeubles (0,70). Le rapport eau/poudre variait entre 0,28 et 0,70. Lors des essais en grandeur nature, le comportement démontrait un important écaillage au feu pour le béton conservé sous eau ayant un rapport eau/poudre<0,40 et pour le béton conservé à l'air d'un rapport eau/poudre<0.35. Un moyen d'évier cet écaillage a été d'incorporer dans les compositions, des fibres de polypropylène choisies pour leur haute performance. Les résultats en laboratoire sur des cylindres de petites dimensions ont indiqué un comportement similaire du matériau pour le béton auto-compactant et le béton vibré à haute température et il ne s'est pas produit d'écaillage. Ce projet a été réalisé entre 1999 et 2002.
Fire resistance of self-compacting concrete, SCC
Abstract This article outlines laboratory and full-scale studies on fire resistance of SCC. For this purpose 40 pre-stressed columns and 140 cylinders of concrete were subjected to compressive loading at high temperature. The SCC included water-binder ratios, w/b, between 0.40 and 0.70 and large amount limestone powder. Comparison was done with vibrated concrete, VC, with the same w/b. Mix proportions were chosen as regards tunnel concrete (w/b=0.40), prefabricated concrete (w/b=0.55) and concrete for production of dwelling houses (w/b=0.70). The waterpowder ratio, w/p varied between 0.28 and 0.70. The fullscale behaviour showed extensive fire spalling for water-cured concrete at w/p<0.40 and for air-cured concrete at w/p<0.35. One way of avoiding the fire spalling was to introduce polypropylene fibres, PPF, in the mix proportions, which was chosen to be very effective. The laboratory results on small cylinders indicated similar material behaviour of SCC and VC at high temperature when spalling did not occur. The project was performed 1999–2002.
Résumé Cet article traite des études en laboratoire et des essais en grandeur nature sur la résistance au feu du béton autocompactant. Pour cette étude, plus de 40 poutres précontraintes et 140 cylindees ont été soumis à des charges compressives à haute température. Le béton présentait un rapport eau/liant se situant entre 0.40 et 0,70 et contenait une forte proportion de poudre de pierre à chaux. Des comparaisons ont été effectuées avec des bétons vibrés ayant le même rapport eau/liant. Les compositions ont été choisies en fonction du béton destiné à la construction de tunnels (0,40), de celui pour la construction préfabriquée (0,55) et du béton destiné à la production d'immeubles (0,70). Le rapport eau/poudre variait entre 0,28 et 0,70. Lors des essais en grandeur nature, le comportement démontrait un important écaillage au feu pour le béton conservé sous eau ayant un rapport eau/poudre<0,40 et pour le béton conservé à l'air d'un rapport eau/poudre<0.35. Un moyen d'évier cet écaillage a été d'incorporer dans les compositions, des fibres de polypropylène choisies pour leur haute performance. Les résultats en laboratoire sur des cylindres de petites dimensions ont indiqué un comportement similaire du matériau pour le béton auto-compactant et le béton vibré à haute température et il ne s'est pas produit d'écaillage. Ce projet a été réalisé entre 1999 et 2002.
Fire resistance of self-compacting concrete, SCC
Persson, B. (author)
Materials and Structures ; 37 ; 575-584
2004-11-01
10 pages
Article (Journal)
Electronic Resource
English
Fire resistance of self-compacting concrete, SCC
| British Library Online Contents | 2004
Fire resistance of self-compacting concrete, SCC
| Online Contents | 2004
Fire resistance of self-compacting concrete, SCC
| Online Contents | 2004
Fire spalling of self-compacting concrete
| British Library Conference Proceedings | 2007
Self-Compacting Concrete Exposed to Fire
| British Library Conference Proceedings | 2003