Concrete carbonation in arid climate
Abstract Fifty-four different concrete mixes were exposed to hot arid weather in Kuwait to monitor their extent of carbonation. Various parameters affecting carbonation such as water/cement ratio, cement content, type of cement, type and dosage of admixture, water-curing period, type of coating, and the addition of silica fume or pulverized fuel ash were investigated. For many of these variables, the carbonation depth and rate constant (K) are reported for an exposure period of 8.6 years. The results show that the water/cement ratio is one of the main factors affecting carbonation. The values of (K) ranged from 2.1 to 7.8 as the water/cement ratio increased from 0.45 to 0.8. Concrete made with white Portland cement carbonated less than ordinary or sulphate resisting cements. Two curing compounds were effective in reducing carbonation while two coating materials prevented carbonation after eight years of exposure.
Résumé Cinquante-quatre mélanges de béton ont été exposés au dimat aride de Koweit. Les résultats de la carbonatation après 8,6 années d'exposition sont présentés. Divers paramètres affectant la carbonatation sont signalés, comme le rapport eau/ciment, la composition du ciment, le type de ciment, le type et le dosage du mélange, la période d'humidification, le type d'enrobage et l'addition de fumée de silice ou de cendres volantes. Le degré de carbonatation ainsi que la constante (K) sont indiqués pour plusieurs paramètres. Les résultats montrent que le rapport eau/ciment est l'un des facteurs les plus importants affectant la carbonation. Les valeurs de (K) ont varié de 2,1 à 7,8 lorsque le rapport eau/ciment est passé de 0,45 à 0,8. Le béton fait avec du ciment Portland blanc a eu moins de carbonatation que le ciment ordinaire ou le ciment résistant aux sulfates. Deux produits de cure ont réduit avec efficacité la carbonatation tandis que deux matériaux d'enrobage l'ont empêchée après huit années d'exposition.
Concrete carbonation in arid climate
Abstract Fifty-four different concrete mixes were exposed to hot arid weather in Kuwait to monitor their extent of carbonation. Various parameters affecting carbonation such as water/cement ratio, cement content, type of cement, type and dosage of admixture, water-curing period, type of coating, and the addition of silica fume or pulverized fuel ash were investigated. For many of these variables, the carbonation depth and rate constant (K) are reported for an exposure period of 8.6 years. The results show that the water/cement ratio is one of the main factors affecting carbonation. The values of (K) ranged from 2.1 to 7.8 as the water/cement ratio increased from 0.45 to 0.8. Concrete made with white Portland cement carbonated less than ordinary or sulphate resisting cements. Two curing compounds were effective in reducing carbonation while two coating materials prevented carbonation after eight years of exposure.
Résumé Cinquante-quatre mélanges de béton ont été exposés au dimat aride de Koweit. Les résultats de la carbonatation après 8,6 années d'exposition sont présentés. Divers paramètres affectant la carbonatation sont signalés, comme le rapport eau/ciment, la composition du ciment, le type de ciment, le type et le dosage du mélange, la période d'humidification, le type d'enrobage et l'addition de fumée de silice ou de cendres volantes. Le degré de carbonatation ainsi que la constante (K) sont indiqués pour plusieurs paramètres. Les résultats montrent que le rapport eau/ciment est l'un des facteurs les plus importants affectant la carbonation. Les valeurs de (K) ont varié de 2,1 à 7,8 lorsque le rapport eau/ciment est passé de 0,45 à 0,8. Le béton fait avec du ciment Portland blanc a eu moins de carbonatation que le ciment ordinaire ou le ciment résistant aux sulfates. Deux produits de cure ont réduit avec efficacité la carbonatation tandis que deux matériaux d'enrobage l'ont empêchée après huit années d'exposition.
Concrete carbonation in arid climate
Al-Khayat, H. (author) / Haque, M. N. (author) / Fattuhi, N. I. (author)
Materials and Structures ; 35 ; 421-426
2002-08-01
6 pages
Article (Journal)
Electronic Resource
English
Concrete carbonation in arid climate
| British Library Online Contents | 2002
TECHNICAL REPORTS - Concrete carbonation in arid climate
| Online Contents | 2002
Carbonation of Concrete Exposed to Hot and Arid Climate
| Online Contents | 2002
Carbonation of Concrete Exposed to Hot and Arid Climate
| British Library Online Contents | 2002
Climate change-induced carbonation of concrete infrastructure
| Online Contents | 2014