Evolution of Adhesion Deterioration Between Rendering Mortar and Concrete Under Thermal Fatigue Test
Debonding stands as the most severe form of deterioration in facade cladding systems. Accurately understanding its evolution path is paramount for effective maintenance strategies. This study examines the debonding evolution of mortar-concrete adhesion systems under thermal loading, combining periodic bond strength tests and continuous strain monitoring. Results reveal an “S-shaped” decay in degradation paths, delineated into stages of degradation, stagnation, and further degradation. Debonding progression is characterized by instability, with damage accumulating before a threshold, followed by propagating rapidly. Monitoring strain behavior captures the transition of adhesion from healthy to damage stages, with adhesion failure evident in the loss of movement followability.
Evolution of Adhesion Deterioration Between Rendering Mortar and Concrete Under Thermal Fatigue Test
Debonding stands as the most severe form of deterioration in facade cladding systems. Accurately understanding its evolution path is paramount for effective maintenance strategies. This study examines the debonding evolution of mortar-concrete adhesion systems under thermal loading, combining periodic bond strength tests and continuous strain monitoring. Results reveal an “S-shaped” decay in degradation paths, delineated into stages of degradation, stagnation, and further degradation. Debonding progression is characterized by instability, with damage accumulating before a threshold, followed by propagating rapidly. Monitoring strain behavior captures the transition of adhesion from healthy to damage stages, with adhesion failure evident in the loss of movement followability.
Evolution of Adhesion Deterioration Between Rendering Mortar and Concrete Under Thermal Fatigue Test
Lecture Notes in Civil Engineering
Casini, Marco (editor) / Zhang, Peiyi (author)
International Civil Engineering and Architecture Conference ; 2024 ; Seoul, Korea (Republic of)
Proceedings of the 4th International Civil Engineering and Architecture Conference ; Chapter: 34 ; 417-427
2024-11-20
11 pages
Article/Chapter (Book)
Electronic Resource
English
MORTAR PLATE AND CEMENT MORTAR COMPOSITION FOR CONCRETE DETERIORATION DIAGNOSIS
| European Patent Office | 2022
Deterioration of mortar and concrete by pollutant gases
| British Library Conference Proceedings | 1996
Deterioration of CA mortar filling layer under cyclical thermal loading
| Elsevier | 2020
Adhesion between fresh polymethyl methacrylate mortar and fresh cement mortar or concrete
| British Library Conference Proceedings | 1999
The adhesion of mortar and concrete
| Engineering Index Backfile | 1909