Fracture failure of asphalt binder in mixed mode (Modes I and II) by using phase-field model
In the pavement industry, asphalt binder fracture failure is one serious problem that may be caused by excessive loading. In the state-of-the-art research of asphalt cracking, pure single mode cracking, especially Mode I has been studied by many researchers. However, there is a lack of theoretical and experimental research on the mixed-mode cracking, which is more reasonable and realistic. In this paper, a new approach, namely, the phase-field method (PFM) is presented for modelling the mixed mode (Modes I and II) cracking failure in the asphalt binder. The traditional way is to use the Griffith's theory for analysing the initiation and propagation of cracks. Our PFM model describes the whole cracking system using a phase-field variable which assumes a negative one in the void region and a positive one in the solid region. Considering the fact that asphalt is brittle when the temperature is below the glass transition temperature, the fracture toughness is considered as the material property and modelled as the surface energy stored in the diffuse interface between the intact solid and the crack void. The non-conserved Allen–Cahn equation is adopted to evolve the phase-field variable to account for the growth of cracks. The energy-based formulation of the PFM handles the competition between the growth of the surface energy and the release of elastic energy in a natural way: the crack propagation is a result of the energy minimisation in the direction of the steepest descent. Both the linear elasticity and phase-field equation are solved in a unified finite element framework, which is implemented in the commercial software COMSOL. The mixed mode cracking experiment is then performed for validation. It is discovered that PFM can give a good result in predicting the onset of crack propagation.
Fracture failure of asphalt binder in mixed mode (Modes I and II) by using phase-field model
In the pavement industry, asphalt binder fracture failure is one serious problem that may be caused by excessive loading. In the state-of-the-art research of asphalt cracking, pure single mode cracking, especially Mode I has been studied by many researchers. However, there is a lack of theoretical and experimental research on the mixed-mode cracking, which is more reasonable and realistic. In this paper, a new approach, namely, the phase-field method (PFM) is presented for modelling the mixed mode (Modes I and II) cracking failure in the asphalt binder. The traditional way is to use the Griffith's theory for analysing the initiation and propagation of cracks. Our PFM model describes the whole cracking system using a phase-field variable which assumes a negative one in the void region and a positive one in the solid region. Considering the fact that asphalt is brittle when the temperature is below the glass transition temperature, the fracture toughness is considered as the material property and modelled as the surface energy stored in the diffuse interface between the intact solid and the crack void. The non-conserved Allen–Cahn equation is adopted to evolve the phase-field variable to account for the growth of cracks. The energy-based formulation of the PFM handles the competition between the growth of the surface energy and the release of elastic energy in a natural way: the crack propagation is a result of the energy minimisation in the direction of the steepest descent. Both the linear elasticity and phase-field equation are solved in a unified finite element framework, which is implemented in the commercial software COMSOL. The mixed mode cracking experiment is then performed for validation. It is discovered that PFM can give a good result in predicting the onset of crack propagation.
Fracture failure of asphalt binder in mixed mode (Modes I and II) by using phase-field model
Hou, Yue (author) / Yue, Pengtao (author) / Xin, Qiang (author) / Pauli, Troy (author) / Sun, Wenjuan (author) / Wang, Linbing (author)
Road Materials and Pavement Design ; 15 ; 167-181
2014-01-02
15 pages
Article (Journal)
Electronic Resource
English
Fracture failure of asphalt binder in mixed mode (Modes I and II) by using phase-field model
| British Library Online Contents | 2014
Modeling Mode I Cracking Failure in Asphalt Binder by Using Nonconserved Phase-Field Model
| Online Contents | 2014
Modeling Mode I Cracking Failure in Asphalt Binder by Using Nonconserved Phase-Field Model
| British Library Online Contents | 2014
Fracture failure in crack interaction of asphalt binder by using a phase field approach
| Online Contents | 2014