Effect of mechanical properties using different filler metals on wide-clearance activated-diffusion-brazed Ni-based superalloy
The investigation of mechanical properties and failure mechanism of activated-diffusion-brazed (ADB) joints in IN-738 plate were conducted. Joints of this type, which had wide clearance, were formed using the brazing alloys Nicrobraz 150 and DF4B. The microstructural characterization showed that chromium borides with a blocky morphology were present in joints associated with the two brazing alloys. A major difference in matrix phase chemistry was observed, however, for the two brazing alloys, e.g., an Ni-B eutectic phase was observed in Nicrobraz 150, but DF4B exhibited a coarsened gamma prime (gamma) phase and an absence of a nickel boride matrix phase. Results of tensile test showed that ADB specimens using DF4B brazing alloy exhibited 95% nominal tensile strength of IN-738 base materials. Fracture cracks in the joint area were initiated and confined to dispersed chromium boride sites. However, tensile test of ADB specimens using Nicrobraz 150 showed poor tensile properties at all testing temperatures, and their fractures were initiated at a brittle nickel boride site and propagated along the weak-bonded interface between the Ni-B eutectic phase and base materials.
Effect of mechanical properties using different filler metals on wide-clearance activated-diffusion-brazed Ni-based superalloy
The investigation of mechanical properties and failure mechanism of activated-diffusion-brazed (ADB) joints in IN-738 plate were conducted. Joints of this type, which had wide clearance, were formed using the brazing alloys Nicrobraz 150 and DF4B. The microstructural characterization showed that chromium borides with a blocky morphology were present in joints associated with the two brazing alloys. A major difference in matrix phase chemistry was observed, however, for the two brazing alloys, e.g., an Ni-B eutectic phase was observed in Nicrobraz 150, but DF4B exhibited a coarsened gamma prime (gamma) phase and an absence of a nickel boride matrix phase. Results of tensile test showed that ADB specimens using DF4B brazing alloy exhibited 95% nominal tensile strength of IN-738 base materials. Fracture cracks in the joint area were initiated and confined to dispersed chromium boride sites. However, tensile test of ADB specimens using Nicrobraz 150 showed poor tensile properties at all testing temperatures, and their fractures were initiated at a brittle nickel boride site and propagated along the weak-bonded interface between the Ni-B eutectic phase and base materials.
Effect of mechanical properties using different filler metals on wide-clearance activated-diffusion-brazed Ni-based superalloy
Su, C.Y. (author) / Chou, C.P. (author) / Chang, W.J. (author) / Liu, M.H. (author)
Journal of Materials Engineering and Performance ; 9 ; 663-668
2000
6 Seiten, 14 Quellen
Article (Journal)
English
| British Library Online Contents | 2005
| British Library Online Contents | 2005
| British Library Online Contents | 1999
| British Library Online Contents | 2006
| British Library Online Contents | 2010