Fabrication of fine mullite powders by alpha-Al(OH)3-SiO2 core-shell structure precursors
In order to obtain fine mullite powders by a simple and inexpensive process, alpha aluminum hydroxide (alpha-Al(OH)3) was used as raw material, and heterogeneous nucleation-and-growth process was chosen for the preparation of powders. Composite coating particles consisting of alpha-Al(OH)3 cores with outer amorphous silica shell were prepared by heterogeneous nucleation-and-growth process in the ethanol suspension containing ammonia, tetraethylorthosilicate (TEOS) and alpha-Al(OH)3. Fine mullite powders (average particle size 0.67 my m) were fabricated by calcined composite coating particles at 1500 degree C for 2 h.
Fabrication of fine mullite powders by alpha-Al(OH)3-SiO2 core-shell structure precursors
In order to obtain fine mullite powders by a simple and inexpensive process, alpha aluminum hydroxide (alpha-Al(OH)3) was used as raw material, and heterogeneous nucleation-and-growth process was chosen for the preparation of powders. Composite coating particles consisting of alpha-Al(OH)3 cores with outer amorphous silica shell were prepared by heterogeneous nucleation-and-growth process in the ethanol suspension containing ammonia, tetraethylorthosilicate (TEOS) and alpha-Al(OH)3. Fine mullite powders (average particle size 0.67 my m) were fabricated by calcined composite coating particles at 1500 degree C for 2 h.
Fabrication of fine mullite powders by alpha-Al(OH)3-SiO2 core-shell structure precursors
Tang, YueFeng (author) / Lu, Yinong (author) / Li, Aidong (author) / Li, Xiaoyun (author) / Shi, ShuZhe (author) / Ling, Zhi-Da (author)
Applied Surface Science ; 202 ; 211-217
2002
7 Seiten, 12 Quellen
Article (Journal)
English
Fabrication of fine mullite powders by a-Al(OH)3-SiO2 core-shell structure precursors
| British Library Online Contents | 2002
Fabrication of nanocomposite powders with a core-shell structure
| British Library Online Contents | 2019
Microstructures of mullite and mullite-alumina composite sintered from diphasic precursors
| British Library Online Contents | 2001
Hydrothermal Synthesis of Nanosized Mullite Powders
| British Library Online Contents | 2008
Fabrication and nonlinear optical investigations of SiO2@Ag core-shell nanoparticles
| British Library Online Contents | 2017