Water scale on heat transfer surfaces is an important problem during heat transfer to water. In this paper, a graded electroless Ni-Cu-P-PTFE composite coating with non-stick and corrosion-resistant properties was applied to reduce the formation of CaSO4 deposits on the heat transfer surfaces. The effects of the concentrations of Cu2+, cationic surfactant and PTFE in the plating solution on the coating rate and the PTFE content in the coatings were investigated. The thickness and the compositions of the coatings were measured using a digital micrometer and an energy dispersive X-ray microanalysis (EDX), respectively. Surface morphology of the coatings was analysed by a scanning electron microscope (SEM). The experimental results showed that the Ni-Cu-P-PTFE coatings inhibited the formation of CaSO4 scale on the heat transfer surfaces significantly.
Water scale on heat transfer surfaces is an important problem during heat transfer to water. In this paper, a graded electroless Ni-Cu-P-PTFE composite coating with non-stick and corrosion-resistant properties was applied to reduce the formation of CaSO4 deposits on the heat transfer surfaces. The effects of the concentrations of Cu2+, cationic surfactant and PTFE in the plating solution on the coating rate and the PTFE content in the coatings were investigated. The thickness and the compositions of the coatings were measured using a digital micrometer and an energy dispersive X-ray microanalysis (EDX), respectively. Surface morphology of the coatings was analysed by a scanning electron microscope (SEM). The experimental results showed that the Ni-Cu-P-PTFE coatings inhibited the formation of CaSO4 scale on the heat transfer surfaces significantly.
Investigation of graded Ni-Cu-P-PTFE composite coatings with antiscaling properties
Applied Surface Science ; 229 ; 56-62
2004
7 Seiten, 12 Quellen
Article (Journal)
English
Verbundwerkstoff , Nickelverbindung , Beschichtung (Überzug) , stromloses Beschichten , mechanische Festigkeit , Adhäsion , Wärmeleitfähigkeit , Verschleißfestigkeit , oberflächenaktiver Stoff , Rasterelektronenmikroskopie , energiedispersive Spektrometrie , kationisches Tensid , Grenzflächenenergie
Investigation of graded Ni-Cu-P-PTFE composite coatings with antiscaling properties
| British Library Online Contents | 2004
Synthesis, Anticorrosion and Antiscaling Properties of Oxidized Phosphated Starch
| British Library Online Contents | 2001
Simultaneous Use of Polyphosphate for Sequestration and Antiscaling
| American Chemical Society | 2024
Tribological properties of electrodeposited Ni-Co-PTFE composite coatings
| British Library Online Contents | 2007