Corrosion of zinc-coated reinforcing bars in tropical humid marine environments: Fid-Bau Portal

Corrosion of zinc-coated reinforcing bars in tropical humid marine environments

Maldonado, L. / Pech-Canul, M.A. / Alhassan, Safaa

Purpose - Reinforcing steel bars in concrete structures exposed to tropical marine atmospheres experience very high corrosion rates due to several environmental factors. The aim of this research was mainly to elucidate if zinc-coated rebars may delay the onset of corrosion and/or extend the service life of infrastructure in the tropics, as the approach is promising in other atmospheres. Design/methodology/approach - Hot-dip zinc-coated and plain steel rebars were embedded in concrete cylinders made with local aggregates and having four different water-to-cement ratios. Samples were exposed during 24 months at the marine breeze in a coastal site in the Gulf of Mexico. The corrosion behaviour of zinc-coated and uncoated rebars was monitored by means of corrosion potential and linear polarization resistance techniques. Also, carbonation penetration and the chloride ingress were measured and correlated with the corrosion behaviour. Findings - Only under the worst case conditions (concrete with 0.7 w/c ratio) did galvanized steel experience corrosion initiation. It was shown to resist higher chloride levels than uncoated steel and extended the onset of corrosion. Originality/Value - The effectiveness of the zinc-coated bar for corrosion control is controversial and its use mainly is supported by accelerated tests or application in cold or subtropical environments. This research showed the corrosion behaviour in an extremely corrosive tropical zone.