A qualitative test that mimics the corrosion behaviour of metals in contact with treated wood without using wood specimens would be of great value in rapidly evaluating the corrosiveness of new wood preservatives. The objective of this study was to determine whether the linear polarisation resistance of metals immersed in a solution of preservative chemicals is related to corrosion of metals in wood. This technique was used to measure the corrosion rate of four types of metals in three different aqueous solutions of wood preservatives. The four metals were UNS G10180 (SAE 1018 steel), UNS S30400 (AISI 304 stainless steel), UNS S43000 (AISI 430 stainless steel), and UNS Z15001 (zinc). The metals were subjected to various concentrations of alkaline copper quat (ACQ-D), ammoniacal copper citrate (CC), and chromated copper arsenate type C (CCA-C). It was found that the corrosion of metals in the solutions of the wood preservatives did not correlate well to what is known about the corrosion of metals in contact with wood.
Direct current testing to measure corrosiveness of wood preservatives
A qualitative test that mimics the corrosion behaviour of metals in contact with treated wood without using wood specimens would be of great value in rapidly evaluating the corrosiveness of new wood preservatives. The objective of this study was to determine whether the linear polarisation resistance of metals immersed in a solution of preservative chemicals is related to corrosion of metals in wood. This technique was used to measure the corrosion rate of four types of metals in three different aqueous solutions of wood preservatives. The four metals were UNS G10180 (SAE 1018 steel), UNS S30400 (AISI 304 stainless steel), UNS S43000 (AISI 430 stainless steel), and UNS Z15001 (zinc). The metals were subjected to various concentrations of alkaline copper quat (ACQ-D), ammoniacal copper citrate (CC), and chromated copper arsenate type C (CCA-C). It was found that the corrosion of metals in the solutions of the wood preservatives did not correlate well to what is known about the corrosion of metals in contact with wood.
Direct current testing to measure corrosiveness of wood preservatives
Gleichstromversuch zur Messung der Korrosivität von Holzschutzmitteln
Zelinka, Samuel L. (author) / Rammer, Douglas R. (author) / Stone, Donald S. (author) / Gilbertson, James T. (author)
Corrosion Science ; 49 ; 1673-1685
2007
13 Seiten, 4 Bilder, 3 Tabellen, 23 Quellen
Article (Journal)
English
Korrosionsprüfung , potentiostatische Prüfung , qualitative Analyse , Aggressivität , Holzschutzmittel , nichtrostender Stahl , unlegierter Stahl , Zink , Korrosionsgeschwindigkeit , Citrat , Arsenat , Kupferverbindung , pH-Einfluss , alkalisches Medium , saures Medium , neutrales Medium , Chrom-Nickel-Stahl , Chromstahl
Direct current testing to measure corrosiveness of wood preservatives
| British Library Online Contents | 2007
Testing Soil for Corrosiveness
| British Library Online Contents | 1993
CORROSIVENESS EVALUATION DEVICE AND CORROSIVENESS EVALUATION METHOD
| European Patent Office | 2023
Role of Wood Extractives in Black Liquor Corrosiveness
| British Library Online Contents | 2006