Impact of impregnation with boron compounds on the surface hardness and abrasion resistance of some varnished woods
This study was performed to determine the impact of impregnation with boron compounds on the surface hardness and abrasion resistance of some varnished woods. For this purpose, test specimens prepared from Oriental beech, White oak, Scotch pine, and Uludag fir, which met the requirements of ASTM D 358, were impregnated according to ASTM D 1413-99 with boric acid (Ba), borax (Bx), and boric acid + borax (Ba+Bx) by the vacuum technique. After impregnation, the surfaces are coated with synthetic (Sn), water-borne (Wb) and acid hardening (Ah) varnishes in accordance with ASTM D 3023. the surface hardness of specimens after the varnishing process was determined in accordance with ASTM D 4366. The abrasion resistance of specimens after the varnishing process was determined in accordance with TS 4755. According to the wood type, impregnation material and varnish type, the surface hardness was the highest for Oriental beech impregnated with borax + boric acid and acid hardening varnish and the lowest for Uludag fir impregnated with borax + boric acid and synthetic varnish. According to the wood type, impregnation material and varnish type, the abrasion resistance was the highest for Oriental beech impregnated with borax + boric acid and acid hardening varnish and the lowest for Scotch pine impregnated with borax + boric acid and synthetic varnish. Those results should be taken into account for applications like parquet, flooring etc., where the surface hardness and abrasion resistance values are very important.
Impact of impregnation with boron compounds on the surface hardness and abrasion resistance of some varnished woods
This study was performed to determine the impact of impregnation with boron compounds on the surface hardness and abrasion resistance of some varnished woods. For this purpose, test specimens prepared from Oriental beech, White oak, Scotch pine, and Uludag fir, which met the requirements of ASTM D 358, were impregnated according to ASTM D 1413-99 with boric acid (Ba), borax (Bx), and boric acid + borax (Ba+Bx) by the vacuum technique. After impregnation, the surfaces are coated with synthetic (Sn), water-borne (Wb) and acid hardening (Ah) varnishes in accordance with ASTM D 3023. the surface hardness of specimens after the varnishing process was determined in accordance with ASTM D 4366. The abrasion resistance of specimens after the varnishing process was determined in accordance with TS 4755. According to the wood type, impregnation material and varnish type, the surface hardness was the highest for Oriental beech impregnated with borax + boric acid and acid hardening varnish and the lowest for Uludag fir impregnated with borax + boric acid and synthetic varnish. According to the wood type, impregnation material and varnish type, the abrasion resistance was the highest for Oriental beech impregnated with borax + boric acid and acid hardening varnish and the lowest for Scotch pine impregnated with borax + boric acid and synthetic varnish. Those results should be taken into account for applications like parquet, flooring etc., where the surface hardness and abrasion resistance values are very important.
Impact of impregnation with boron compounds on the surface hardness and abrasion resistance of some varnished woods
Atar, Musa (author) / Uysal, Burhanettin (author) / Sarica, Mutlu (author)
Journal of Applied Polymer Science ; 114 ; 204-211
2009
8 Seiten, 7 Tabellen, 24 Quellen
Article (Journal)
English
Impact of impregnation with boron compounds on the surface hardness of varnished wood
Tema Archive | 2007
|European Patent Office | 2015
|The preservation of woods by the new methods of impregnation
Engineering Index Backfile | 1907
|Surface Roughness of Varnished Wood Pre-Treated Using Sanding and Thermal Compression
DOAJ | 2022
|