Anodic corrosion inhibitors against chloride induced corrosion of concrete rebars
The effect of anodic inhibitors [calcium nitrate Ca(NO3)2, calcium nitrite Ca(NO2)2 and potassium nitrite NaNO2] has been evaluated using cylinders with steel rebars exposed to the following environments: in the marine tidal zone, at roof top and in air of 38 deg C and 90% relative humidity for 4 years. The experiments showed that the half cell potentials were more negative than the visual inspections proved when anodic inhibitors are used. Inhibitor dosage on 3-4% of cement weight seems sufficient to protect the rebar against corrosion. Capillary absorption experiments showed that the concrete porosity was unaffected by the inhibitors. The concentration profiles of chloride, nitrite and nitrate were investigated with respect to leaching. However, it was difficult to find the background level of nitrite due to possible chemical alteration.
Anodic corrosion inhibitors against chloride induced corrosion of concrete rebars
The effect of anodic inhibitors [calcium nitrate Ca(NO3)2, calcium nitrite Ca(NO2)2 and potassium nitrite NaNO2] has been evaluated using cylinders with steel rebars exposed to the following environments: in the marine tidal zone, at roof top and in air of 38 deg C and 90% relative humidity for 4 years. The experiments showed that the half cell potentials were more negative than the visual inspections proved when anodic inhibitors are used. Inhibitor dosage on 3-4% of cement weight seems sufficient to protect the rebar against corrosion. Capillary absorption experiments showed that the concrete porosity was unaffected by the inhibitors. The concentration profiles of chloride, nitrite and nitrate were investigated with respect to leaching. However, it was difficult to find the background level of nitrite due to possible chemical alteration.
Anodic corrosion inhibitors against chloride induced corrosion of concrete rebars
Anodische Korrosionsinhibitoren gegen Chlorid-induzierte Korrosion von Betonstählen
Ostnor, T.A. (author) / Justnes, H. (author)
Advances in Applied Ceramics ; 110 ; 131-136
2010
6 Seiten, 9 Bilder, 4 Tabellen, 25 Quellen
Article (Journal)
English
Calcium Nitrate as Inhibitor against Chloride Induced Corrosion of Concrete Rebars
| British Library Conference Proceedings | 2002
Effect of binary mixtures on chloride induced corrosion of rebars in concrete
| BASE | 2018
Corrosion Products of Galvanized Rebars Embedded in Chloride-Contaminated Concrete
| British Library Online Contents | 2000
Corrosion products of galvanized rebars embedded in chloride-contaminated concrete
| Tema Archive | 2000
Corrosion initiation state of rebars in concrete subjected to chloride penetration
| British Library Conference Proceedings | 2010