Evaluation of Recycled Aggregate Concrete Cracking through Ring Test
Cracks can reduce the service life of a concrete structure by allowing aggressive agents to penetrate through it in easy ways. Free shrinkage evaluation alone is not enough to determine if cracking can be expected in a structure since concrete creep behaviour, stiffness and toughness also influence the potential for cracking. Consequently, it is rather interesting to perform restrained shrinkage tests, such as the ring test according to ASTM C 1581–04. The testing procedure involves concrete ring specimens restrained by an inner steel ring on which strain gauges are placed to determine the age of cracking, since abrupt changes in the steel strain occur when concrete is cracked. Both the ring test and free shrinkage test should be carried out in the same exposure conditions, 21°C and 50% relative humidity. Moreover, compressive and tensile strengths of concrete were evaluated on cubic specimens at the time of its cracking and up to 28 days of curing. By means of analytical and numerical models of the ring specimen, some useful information on the stress induced in the material and on the tensile creep behaviour of concrete can be extrapolated thus allowing to better interpret the experimental results. This experimental procedure enables to study the influence of concrete mixture composition on the potential for early-age cracking of concrete. In particular, in this work the influence on early-age cracking of recycled-concrete aggregate partially replacing virgin sand was tested.
Evaluation of Recycled Aggregate Concrete Cracking through Ring Test
Cracks can reduce the service life of a concrete structure by allowing aggressive agents to penetrate through it in easy ways. Free shrinkage evaluation alone is not enough to determine if cracking can be expected in a structure since concrete creep behaviour, stiffness and toughness also influence the potential for cracking. Consequently, it is rather interesting to perform restrained shrinkage tests, such as the ring test according to ASTM C 1581–04. The testing procedure involves concrete ring specimens restrained by an inner steel ring on which strain gauges are placed to determine the age of cracking, since abrupt changes in the steel strain occur when concrete is cracked. Both the ring test and free shrinkage test should be carried out in the same exposure conditions, 21°C and 50% relative humidity. Moreover, compressive and tensile strengths of concrete were evaluated on cubic specimens at the time of its cracking and up to 28 days of curing. By means of analytical and numerical models of the ring specimen, some useful information on the stress induced in the material and on the tensile creep behaviour of concrete can be extrapolated thus allowing to better interpret the experimental results. This experimental procedure enables to study the influence of concrete mixture composition on the potential for early-age cracking of concrete. In particular, in this work the influence on early-age cracking of recycled-concrete aggregate partially replacing virgin sand was tested.
Evaluation of Recycled Aggregate Concrete Cracking through Ring Test
Corinaldesi, Valeria (author) / Moriconi, Giacomo (author)
2012
6 Seiten
Conference paper
English
Evaluation of Recycled Aggregate Concrete Cracking through Ring Test
| Trans Tech Publications | 2012
Evaluation of Recycled Aggregate Concrete Craking through Ring Test
| British Library Conference Proceedings | 2012
TRANSVERSE CRACKING IN RECYCLED CONCRETE AGGREGATE PAVEMENTS
Online Contents | 1996
Restrained shrinkage cracking of recycled aggregate concrete
| Online Contents | 2017
Restrained shrinkage cracking of recycled aggregate concrete
| Springer Verlag | 2017