Use of Vibrating Wire Strain Gauges to Monitor Corrosion-Induced Deterioration of Concrete
Steel reinforcement corrosion is always one of the most significant incentives of concrete structure deterioration, especially under severe chloride erosion environment. In order to describe the whole process of concrete deterioration induced by reinforcement corrosion, the mechanism of rust expansion and crack propagation in concrete was analyzed from the perspective of elastoplastic mechanics and fracture mechanics firstly, and experimental study was carried out to use vibrating wire strain gauges for monitoring corrosion-induced concrete deterioration process. The mechanism analysis of corrosion-induced concrete deterioration indicates that the degradation process of cover concrete can be divided into aggressive medium transmission process, free corrosive expansion process, corrosive expansion stress development process, corrosive expansion crack generation and propagation process, and vibrating wire strain gauges can be used to monitor corrosion-induced cover concrete stress development, crack initiation and propagation process along with the procedure of reinforcement corrosion. The test curve seems to be generally consistent with that of the theoretic analysis, and the signals captured by vibrating wire strain gauges can successfully reflect the durability degradation process of reinforced concrete structure under severe erosion environment.
Use of Vibrating Wire Strain Gauges to Monitor Corrosion-Induced Deterioration of Concrete
Steel reinforcement corrosion is always one of the most significant incentives of concrete structure deterioration, especially under severe chloride erosion environment. In order to describe the whole process of concrete deterioration induced by reinforcement corrosion, the mechanism of rust expansion and crack propagation in concrete was analyzed from the perspective of elastoplastic mechanics and fracture mechanics firstly, and experimental study was carried out to use vibrating wire strain gauges for monitoring corrosion-induced concrete deterioration process. The mechanism analysis of corrosion-induced concrete deterioration indicates that the degradation process of cover concrete can be divided into aggressive medium transmission process, free corrosive expansion process, corrosive expansion stress development process, corrosive expansion crack generation and propagation process, and vibrating wire strain gauges can be used to monitor corrosion-induced cover concrete stress development, crack initiation and propagation process along with the procedure of reinforcement corrosion. The test curve seems to be generally consistent with that of the theoretic analysis, and the signals captured by vibrating wire strain gauges can successfully reflect the durability degradation process of reinforced concrete structure under severe erosion environment.
Use of Vibrating Wire Strain Gauges to Monitor Corrosion-Induced Deterioration of Concrete
Liu, Xiao-Chun (author) / Wei, Jun (author) / Wang, Zhen-yu (author)
2012
6 Seiten
Conference paper
English
Use of Vibrating Wire Strain Gauges to Monitor Corrosion-Induced Deterioration of Concrete
| British Library Online Contents | 2012
Monitoring the Evolution of Concrete Strain Using Vibrating Wire Strain Gauges
| Springer Verlag | 2023
The Use of Vibrating Wire Strain Gauges in Geotechnics
| British Library Conference Proceedings | 2000
Interpretation of results from vibrating-wire strain gauges in fresh concretes
| Engineering Index Backfile | 1968
| British Library Online Contents | 2003