Interfacial Transition Zone Meso-Structure of MgO Concrete Loaded to Failure by Computed Tomography
The computed tomography was introduced to track the development of cracks in cement matrix and interfacial transition zone of MgO concrete under load to failure. Results indicated that some pores were present before concrete was loaded due to none compaction which would tend to initiate cracks expanding. After loading, energy transferring route kept changing and extended towards weak area and it chose to be released through aggregates when concentrated stress on cracks tip surpassed ultimate load with consequences of some cracks getting interconnected with each other through cement matrix. Differentiated and Binarized CT images analysis confirmed that width of cracks was increased and extending routes diversified with loading implemented and interfacial transition zone remained primary choice for cracks development.
Interfacial Transition Zone Meso-Structure of MgO Concrete Loaded to Failure by Computed Tomography
The computed tomography was introduced to track the development of cracks in cement matrix and interfacial transition zone of MgO concrete under load to failure. Results indicated that some pores were present before concrete was loaded due to none compaction which would tend to initiate cracks expanding. After loading, energy transferring route kept changing and extended towards weak area and it chose to be released through aggregates when concentrated stress on cracks tip surpassed ultimate load with consequences of some cracks getting interconnected with each other through cement matrix. Differentiated and Binarized CT images analysis confirmed that width of cracks was increased and extending routes diversified with loading implemented and interfacial transition zone remained primary choice for cracks development.
Interfacial Transition Zone Meso-Structure of MgO Concrete Loaded to Failure by Computed Tomography
Yang, Hua-Quan (author) / Chen, Xia (author) / Zuo, Yong-Zhen (author)
2012
5 Seiten
Conference paper
English
Interfacial Transition Zone Meso-Structure of MgO Concrete Loaded to Failure by Computed Tomography
| British Library Conference Proceedings | 2013
Durability and Meso Interfacial Transition Zone Optimization of Reinforced Concrete Cover
| British Library Online Contents | 2009
3D meso-scale modelling of foamed concrete based on X-ray Computed Tomography
| British Library Online Contents | 2018
Micro-computed tomography determination of glass fibre reinforced polymer meso-structure
| British Library Online Contents | 2006
Meso-scale framework for modeling granular material using computed tomography
| British Library Online Contents | 2016