Storage Modulus Capacity of Untreated Aged Arenga pinnata Fibre-Reinforced Epoxy Composite
Research on natural fibre is keeps on going due to their high strength and stiffness, natural availability, and environmental friendliness. In addition, they are also recyclable, renewable and low in raw material cost. This study was done to determine the performance of aging Arenga Pinnata fibre-reinforced epoxy composite (APFREC) on varying temperature. The specimens were aged from 0 to 90 days by using accelerated aging process and were subjected to dynamic mechanical analysis (DMA) and flexural modulus evaluation. The results have shown that specimens with lower aging days have higher storage modulus initially, that is at below 70 °C but as the temperature increase, its storage modulus drastically decrease in comparison to a more aged specimen. Result of storage modulus at low temperature is similar flexure modulus evaluation. The research indicates that aging APFREC specimens has better thermal resistance.
Storage Modulus Capacity of Untreated Aged Arenga pinnata Fibre-Reinforced Epoxy Composite
Research on natural fibre is keeps on going due to their high strength and stiffness, natural availability, and environmental friendliness. In addition, they are also recyclable, renewable and low in raw material cost. This study was done to determine the performance of aging Arenga Pinnata fibre-reinforced epoxy composite (APFREC) on varying temperature. The specimens were aged from 0 to 90 days by using accelerated aging process and were subjected to dynamic mechanical analysis (DMA) and flexural modulus evaluation. The results have shown that specimens with lower aging days have higher storage modulus initially, that is at below 70 °C but as the temperature increase, its storage modulus drastically decrease in comparison to a more aged specimen. Result of storage modulus at low temperature is similar flexure modulus evaluation. The research indicates that aging APFREC specimens has better thermal resistance.
Storage Modulus Capacity of Untreated Aged Arenga pinnata Fibre-Reinforced Epoxy Composite
Khalid, Muhamad Faris Syafiq (author) / Abdullah, Abdul Hakim (author)
2013
6 Seiten
Conference paper
English
The effect of aging on Arenga pinnata fiber-reinforced epoxy composite
| Elsevier | 2010
The effect of aging on Arenga pinnata fiber-reinforced epoxy composite
| British Library Online Contents | 2010
Toughness characteristics of Arenga pinnata fibre concrete
| Tema Archive | 2005
Swelling behaviour and morphological analysis of Arenga pinnata–silicone biocomposite
| British Library Online Contents | 2019
| British Library Online Contents | 2011