Influence of Nano-SiO2 and Nano-TiO2 on Early Hydration of Calcium Sulfoaluminate Cement
Calcium sulfoaluminate (CSA) cements were currently receiving a lot of attention because their manufacture produced less CO2 than ordinary Portland cement (OPC). However, it was essential to understand all parameters which might affect the hydration process. This work dealt with the effect of two nanostructured materials, such as nano-SiO2 (NS) and nanoTiO2 (NT), on the properties of CSA pastes during early hydration. Isothermal calorimetry, X-ray diffraction (XRD) and Scanning electron microscopy (SEM) were used to analyze the pastes. Results indicated that the influence of NS and NT on the early hydration of CSA showed different: when NS and NT were added by 5% (mass fraction), the early hydration of CSA cement can be significantly promoted by NS, and slightly accelerated by NT. X-ray diffraction and SEM analysis results showed that both of NS and NT can improve the microstructure of the cement pastes, which made the cement stone more uniform and dense. For the difference, during cement hydration, except for nucleation function, NS had a high pozzolanic activity. Whereas, the effect of NT on microstructure of hardened CSA-cement was mainly due to its seeding effect.
Influence of Nano-SiO2 and Nano-TiO2 on Early Hydration of Calcium Sulfoaluminate Cement
Calcium sulfoaluminate (CSA) cements were currently receiving a lot of attention because their manufacture produced less CO2 than ordinary Portland cement (OPC). However, it was essential to understand all parameters which might affect the hydration process. This work dealt with the effect of two nanostructured materials, such as nano-SiO2 (NS) and nanoTiO2 (NT), on the properties of CSA pastes during early hydration. Isothermal calorimetry, X-ray diffraction (XRD) and Scanning electron microscopy (SEM) were used to analyze the pastes. Results indicated that the influence of NS and NT on the early hydration of CSA showed different: when NS and NT were added by 5% (mass fraction), the early hydration of CSA cement can be significantly promoted by NS, and slightly accelerated by NT. X-ray diffraction and SEM analysis results showed that both of NS and NT can improve the microstructure of the cement pastes, which made the cement stone more uniform and dense. For the difference, during cement hydration, except for nucleation function, NS had a high pozzolanic activity. Whereas, the effect of NT on microstructure of hardened CSA-cement was mainly due to its seeding effect.
Influence of Nano-SiO2 and Nano-TiO2 on Early Hydration of Calcium Sulfoaluminate Cement
Ma, Bao-guo (author) / Li, Hai-Nan (author) / Zhu, Yan-Chao (author) / Han, Lei (author) / Li, Xiang-guo (author)
2014
7 Seiten
Conference paper
English
Influence of Nano-SiO~2 and Nano-TiO~2 on Early Hydration of Calcium Sulfoaluminate Cement
| British Library Online Contents | 2014
Influence of Nano-SiO~2 and Nano-TiO~2 on Early Hydration of Calcium Sulfoaluminate Cement
| British Library Conference Proceedings | 2014
Ternesite-calcium sulfoaluminate cement: Preparation and hydration
| Elsevier | 2022
Influence of sodium borate on the early age hydration of calcium sulfoaluminate cement
| Tema Archive | 2015