Grain boundary microcracking in sliding test using a silicon pin was evaluated on several kinds of AlN to investigate the behavior of damage generation and the influence of material properties on it. The grain boundary fracture toughness (KIC gb ) was estimated from a percentage of the intergranular fracture as a grain boundary property for each specimen. KIC gb was greatly influensed by an amount and kinds of additives. After the sliding test, silicon debris accumulation and grain boundary microcracking of AlN were observed at the wear traces on the surface of AlN. The density of grain boundary microcracks increased linearly with increasing the contact load. Empirical relationship indicated that its density depended on KIC gb and the AlN grain size, and decreased mainly with increasing KIC gb. The density of grain boundary microcracks greatly degreased at the KIC gbvalue above 1.9 (MPa·m1/2).
Influence of Grain Boundary Properties on Microcracking of AlN in Sliding Test
Grain boundary microcracking in sliding test using a silicon pin was evaluated on several kinds of AlN to investigate the behavior of damage generation and the influence of material properties on it. The grain boundary fracture toughness (KIC gb ) was estimated from a percentage of the intergranular fracture as a grain boundary property for each specimen. KIC gb was greatly influensed by an amount and kinds of additives. After the sliding test, silicon debris accumulation and grain boundary microcracking of AlN were observed at the wear traces on the surface of AlN. The density of grain boundary microcracks increased linearly with increasing the contact load. Empirical relationship indicated that its density depended on KIC gb and the AlN grain size, and decreased mainly with increasing KIC gb. The density of grain boundary microcracks greatly degreased at the KIC gbvalue above 1.9 (MPa·m1/2).
Influence of Grain Boundary Properties on Microcracking of AlN in Sliding Test
Key Engineering Materials ; 317-318 ; 441-444
2006-08-15
4 pages
Article (Journal)
Electronic Resource
English
Influence of Grain Boundary Properties on Microcracking of AIN in Sliding Test
| British Library Online Contents | 2006
Microcracking in coarse and fine grain marbles
| British Library Conference Proceedings | 1995
Influence of Microcracking on Shear Localization
| Online Contents | 2011
| British Library Online Contents | 2008
| British Library Online Contents | 2010