High Temperature Behavior of Salt Coated Nicalon Fiber Reinforced Calcium Aluminosilicate Composite
The effects of molten salt (sodium sulfate) on the high temperature mechanical behavior of Nicalon SiC fiber reinforced calcium aluminosilicate are investigated in this study. Tensile specimens were coated with sodium sulfate and exposed at 900°C for 100 hours and then tested at 900°C. It has been shown that the strength of the composite was reduced due to salt induced oxidation embrittlement. The synergistic effect of matrix cracking and hot corrosion was also investigated. Strength was dramatically decreased in specimens which were preloaded and then exposed at elevated temperature. However, specimens which were preloaded prior to the hot corrosion exposure retained more of their strength than the specimens which experienced the same preload and heat‐treatment with no salt. Possible degradation mechanisms of these specimens are discussed.
High Temperature Behavior of Salt Coated Nicalon Fiber Reinforced Calcium Aluminosilicate Composite
The effects of molten salt (sodium sulfate) on the high temperature mechanical behavior of Nicalon SiC fiber reinforced calcium aluminosilicate are investigated in this study. Tensile specimens were coated with sodium sulfate and exposed at 900°C for 100 hours and then tested at 900°C. It has been shown that the strength of the composite was reduced due to salt induced oxidation embrittlement. The synergistic effect of matrix cracking and hot corrosion was also investigated. Strength was dramatically decreased in specimens which were preloaded and then exposed at elevated temperature. However, specimens which were preloaded prior to the hot corrosion exposure retained more of their strength than the specimens which experienced the same preload and heat‐treatment with no salt. Possible degradation mechanisms of these specimens are discussed.
High Temperature Behavior of Salt Coated Nicalon Fiber Reinforced Calcium Aluminosilicate Composite
Wachtman, John B. Jr. (editor) / Wang, S.‐W. (author) / Kowalik, R. W. (author) / Sands, R. (author)
1994-01-01
10 pages
Article/Chapter (Book)
Electronic Resource
English
| British Library Online Contents | 1995
| British Library Online Contents | 1998
Stability of interfaces in calcium aluminosilicate matrix/Nicalon SiC fibre composites
| British Library Online Contents | 1993
Thermal-shock behavior of a Nicalon-fiber-reinforced hybrid glass-ceramic composite
| British Library Online Contents | 2001
| British Library Online Contents | 1992