High‐Density Lignin‐Derived Carbon Nanofiber Supercapacitors with Enhanced Volumetric Energy Density
Supercapacitors are increasingly used in short‐distance electric transportation due to their long lifetime (≈15 years) and fast charging capability (>10 A g−1). To improve their market penetration, while minimizing onboard weight and maximizing space‐efficiency, materials costs must be reduced (<10 $ kg−1) and the volumetric energy‐density increased (>8 Wh L−1). Carbon nanofibers display good gravimetric capacitance, yet their marketability is hindered by their low density (0.05–0.1 g cm−3). Here, the authors increase the packing density of low‐cost, free‐standing carbon nanofiber mats (from 0.1 to 0.6 g cm−3) through uniaxial compression. X‐ray computed tomography reveals that densification occurs by reducing the inter‐fiber pore size (from 1–5 µm to 0.2–0.5 µm), which are not involved in double‐layer capacitance. The improved packing density is directly proportional to the volumetric performances of the device, which reaches a volumetric capacitance of 130 F cm−3 and energy density of 6 Wh L−1 at 0.1 A g−1 using a loading of 3 mg cm−2. The results outperform most commercial and lab‐scale porous carbons synthesized from bioresources (50–100 F cm−3, 1–3 Wh L−1 using 10 mg cm−2) and contribute to the scalable design of sustainable electrodes with minimal ‘dead volume’ for efficient supercapacitors.
High‐Density Lignin‐Derived Carbon Nanofiber Supercapacitors with Enhanced Volumetric Energy Density
Supercapacitors are increasingly used in short‐distance electric transportation due to their long lifetime (≈15 years) and fast charging capability (>10 A g−1). To improve their market penetration, while minimizing onboard weight and maximizing space‐efficiency, materials costs must be reduced (<10 $ kg−1) and the volumetric energy‐density increased (>8 Wh L−1). Carbon nanofibers display good gravimetric capacitance, yet their marketability is hindered by their low density (0.05–0.1 g cm−3). Here, the authors increase the packing density of low‐cost, free‐standing carbon nanofiber mats (from 0.1 to 0.6 g cm−3) through uniaxial compression. X‐ray computed tomography reveals that densification occurs by reducing the inter‐fiber pore size (from 1–5 µm to 0.2–0.5 µm), which are not involved in double‐layer capacitance. The improved packing density is directly proportional to the volumetric performances of the device, which reaches a volumetric capacitance of 130 F cm−3 and energy density of 6 Wh L−1 at 0.1 A g−1 using a loading of 3 mg cm−2. The results outperform most commercial and lab‐scale porous carbons synthesized from bioresources (50–100 F cm−3, 1–3 Wh L−1 using 10 mg cm−2) and contribute to the scalable design of sustainable electrodes with minimal ‘dead volume’ for efficient supercapacitors.
High‐Density Lignin‐Derived Carbon Nanofiber Supercapacitors with Enhanced Volumetric Energy Density
Hérou, Servann (author) / Bailey, Josh J (author) / Kok, Matt (author) / Schlee, Philipp (author) / Jervis, Rhodri (author) / Brett, Dan J. L. (author) / Shearing, Paul R. (author) / Ribadeneyra, Maria Crespo (author) / Titirici, Magdalena (author)
Advanced Science ; 8
2021-09-01
11 pages
Article (Journal)
Electronic Resource
English
| British Library Online Contents | 2015
Lignin-based hierarchical porous carbon nanofiber films with superior performance in supercapacitors
| British Library Online Contents | 2018
| British Library Online Contents | 2018