Halloysite reinforced 3D-printable geopolymers
This study investigates the role of halloysite nanotube as a mineral-based thixotropic admixture to 3D printable geopolymer mortar. The first part of this paper focuses on the fundamental characterization of the thermal evolution of halloysite at 30–1000 °C. In the second part, we show how the calcination and concentration of halloysite influence the fresh and hardened properties of 3D-printable geopolymer mortar. It was found that regardless of thermal treatment, using only 1–2 wt.% halloysite can significantly increase the rheological properties and buildability of the mortars without compromising their mechanical strength. However, the setting time of geopolymer only accelerated when highly reactive dehydroxylated halloysite was used. Compared with mold-cast specimens, the mechanical properties of 3D-printed specimens were lower at early ages due to their higher surface dehydration; however, the gap became closer over time.
Halloysite reinforced 3D-printable geopolymers
This study investigates the role of halloysite nanotube as a mineral-based thixotropic admixture to 3D printable geopolymer mortar. The first part of this paper focuses on the fundamental characterization of the thermal evolution of halloysite at 30–1000 °C. In the second part, we show how the calcination and concentration of halloysite influence the fresh and hardened properties of 3D-printable geopolymer mortar. It was found that regardless of thermal treatment, using only 1–2 wt.% halloysite can significantly increase the rheological properties and buildability of the mortars without compromising their mechanical strength. However, the setting time of geopolymer only accelerated when highly reactive dehydroxylated halloysite was used. Compared with mold-cast specimens, the mechanical properties of 3D-printed specimens were lower at early ages due to their higher surface dehydration; however, the gap became closer over time.
Halloysite reinforced 3D-printable geopolymers
Ranjbar, Navid (Autor:in) / Kuenzel, Carsten (Autor:in) / Gundlach, Carsten (Autor:in) / Kempen, Paul (Autor:in) / Mehrali, Mehdi (Autor:in)
01.01.2023
Ranjbar , N , Kuenzel , C , Gundlach , C , Kempen , P & Mehrali , M 2023 , ' Halloysite reinforced 3D-printable geopolymers ' , Cement and Concrete Composites , vol. 136 , 104894 . https://doi.org/10.1016/j.cemconcomp.2022.104894
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Halloysite reinforced 3D-printable geopolymers
| Elsevier | 2022
Rheological characterization of 3D printable geopolymers
| Elsevier | 2021
Effects of halloysite in kaolin on the formation and properties of geopolymers
| Online Contents | 2012