Preparation and photo-electrocatalytic performance of Ag-Ti3+-TiO2 nanocone
The overuse of antibiotics has caused persistent pollution to the environment，and photo-electrocatalysis is an environmentally friendly and efficient technology for degrading antibiotics，in which the design of photoelectrodes is particularly important. To improve the rate of antibiotic degradation，Ag-Ti3+-TiO2 nanocone composite photoelectrode was prepared by electrochemical reduction and photoreduction methods. Then it was used to simulate the photo-electrocatalytic degradation of tetracycline under visible light irradiation to investigate its photocatalytic performance. The results showed that the composite electrode effectively suppressed the complexation of photogenerated electron-hole pairs and exhibited a lower charge transfer resistance to improve the photo-electrocatalytic performance due to the Ti3+ self-doping and the local surface plasmon resonance effect of Ag nanoparticles. The composite photoelectrode degraded 87.9% of tetracycline after 90 min under visible light irradiation，and the degradation rate was maintained at 82.5% after 5 cycles. These results indicated that the Ag-Ti3+-TiO2 nanocone composite photoelectrode had high degradation efficiency，good stability and sustainable recyclability，and was expected to achieve efficient and environmentally friendly photo-electrocatalytic degradation of antibiotics.
Preparation and photo-electrocatalytic performance of Ag-Ti3+-TiO2 nanocone
The overuse of antibiotics has caused persistent pollution to the environment，and photo-electrocatalysis is an environmentally friendly and efficient technology for degrading antibiotics，in which the design of photoelectrodes is particularly important. To improve the rate of antibiotic degradation，Ag-Ti3+-TiO2 nanocone composite photoelectrode was prepared by electrochemical reduction and photoreduction methods. Then it was used to simulate the photo-electrocatalytic degradation of tetracycline under visible light irradiation to investigate its photocatalytic performance. The results showed that the composite electrode effectively suppressed the complexation of photogenerated electron-hole pairs and exhibited a lower charge transfer resistance to improve the photo-electrocatalytic performance due to the Ti3+ self-doping and the local surface plasmon resonance effect of Ag nanoparticles. The composite photoelectrode degraded 87.9% of tetracycline after 90 min under visible light irradiation，and the degradation rate was maintained at 82.5% after 5 cycles. These results indicated that the Ag-Ti3+-TiO2 nanocone composite photoelectrode had high degradation efficiency，good stability and sustainable recyclability，and was expected to achieve efficient and environmentally friendly photo-electrocatalytic degradation of antibiotics.
Preparation and photo-electrocatalytic performance of Ag-Ti3+-TiO2 nanocone
ZHANG Huixia (Autor:in) / XIE Chenxin (Autor:in) / ZHOU Lishan (Autor:in) / REN Chunyan (Autor:in) / ZHAO Hui (Autor:in) / LEI Taiping (Autor:in) / ZHU Lingzhi (Autor:in)
2024
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
Nanocone formation on ion-bombarded InP surfaces
| British Library Online Contents | 2015
Preparation and characterization of the CrN nanocone array textured WS2 film
| British Library Online Contents | 2017
Nanocone formation on ion-bombarded InP surfaces
| British Library Online Contents | 2015
Preparation of nanocone ZnO thin film and its aging effect of photoluminescence
| British Library Online Contents | 2009