Evolution of gases during solidification of 3% Si transformer steel

Moshkevich, E.I.

Theoretical and experimental data are presented to show that, in order to avoid rimming and to obtain sound 10-cm thick surface zone in large ingots of this steel, hydrogen in metal must not exceed 4.0-4.5 cc/100 g if nitrogen is 6-4 cc. (See also Stal n 1 Jan 1963 p 34-7)

Zugriff

Zugriff über TIB

Verfügbarkeit in meiner Bibliothek prüfen

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

Evolution of gases during solidification of 3% Si transformer steel

Moshkevich, E.I.

Theoretical and experimental data are presented to show that, in order to avoid rimming and to obtain sound 10-cm thick surface zone in large ingots of this steel, hydrogen in metal must not exceed 4.0-4.5 cc/100 g if nitrogen is 6-4 cc. (See also Stal n 1 Jan 1963 p 34-7)

Evolution of gases during solidification of 3% Si transformer steel

Moshkevich, E.I.

Theoretical and experimental data are presented to show that, in order to avoid rimming and to obtain sound 10-cm thick surface zone in large ingots of this steel, hydrogen in metal must not exceed 4.0-4.5 cc/100 g if nitrogen is 6-4 cc. (See also Stal n 1 Jan 1963 p 34-7)

Zugriff

Zugriff über TIB

Verfügbarkeit in meiner Bibliothek prüfen

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

Dokumentinformationen

Titel:

Evolution of gases during solidification of 3% Si transformer steel

Weitere Titelangaben:

Likvatsiya gazov pri kristallizatsii nizkouglerodistoi kremnistoi stali

Beteiligte:

Moshkevich, E.I. (Autor:in)

Erschienen in:

Stal in English

Erscheinungsdatum:

1963

Format / Umfang:

3 pages

Medientyp:

Aufsatz (Zeitschrift)

Format:

Print

Sprache:

Englisch

Schlagwörter:

Electric transformers

© Metadata Copyright Elsevier B. V. All rights reserved.

Ähnliche Titel

Evolution of gases during solidification of 3% Si transformer steel

Moshkevich, E.I. | Engineering Index Backfile | 1963

Microstructure evolution in AISI 304 stainless steel during near rapid directional solidification

Fu, J.W. / Yang, Y.S. / Guo, J.J. et al. | British Library Online Contents | 2009

Microstructural evolution in 316LN austenitic stainless steel during solidification process under different cooling rates

Wu, C. / Li, S. / Zhang, C. et al. | British Library Online Contents | 2016

Microstructural evolution in AISI 304 stainless steel during directional solidification and subsequent solid-state transformation

Ma, J. C. / Yang, Y. S. / Tong, W. H. et al. | British Library Online Contents | 2007

Microstructural Evolution during Directional Solidification of Superalloy CMSX-6

Ma, D. / Sahm, P. R. | British Library Online Contents | 1996