Analysis of the S–N curves of welded joints enhanced by ultrasonic peening treatment
Abstract Contrast fatigue tests were carried out on T-shape tubular joints of 20 steel in three conditions: as welded, treated by ultrasonic peening treatment (UPT) before loading and UPT under loading. Results are: (1) Dispersity of test results measured by nominal stress is much larger than that measured by hot spot stress. After UPT before loading, fatigue strength of 20 steel tubular joints measured by hot spot stress increases by 67% and fatigue life is prolonged by 22–45 times. (2) Under low stress ratio R, UPT before loading can improve the fatigue performance of welded tubular joints significantly. (3) Under high stress ratio R, UPT under loading (static load) is recommended to improve the fatigue performance of welded tubular joints. UPT under loading not only enhances the fatigue properties at low stress level, but also at high stress level. (4) The general rule of S–N curves of welded joints treated by UPT is commonly effected by external load (static load) and self release of residual stress.
Analysis of the S–N curves of welded joints enhanced by ultrasonic peening treatment
Abstract Contrast fatigue tests were carried out on T-shape tubular joints of 20 steel in three conditions: as welded, treated by ultrasonic peening treatment (UPT) before loading and UPT under loading. Results are: (1) Dispersity of test results measured by nominal stress is much larger than that measured by hot spot stress. After UPT before loading, fatigue strength of 20 steel tubular joints measured by hot spot stress increases by 67% and fatigue life is prolonged by 22–45 times. (2) Under low stress ratio R, UPT before loading can improve the fatigue performance of welded tubular joints significantly. (3) Under high stress ratio R, UPT under loading (static load) is recommended to improve the fatigue performance of welded tubular joints. UPT under loading not only enhances the fatigue properties at low stress level, but also at high stress level. (4) The general rule of S–N curves of welded joints treated by UPT is commonly effected by external load (static load) and self release of residual stress.
Analysis of the S–N curves of welded joints enhanced by ultrasonic peening treatment
Zhao, Xiaohui (Autor:in) / Wang, Dongpo (Autor:in) / Huo, Lixing (Autor:in)
17.06.2010
9 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Analysis of the S-N curves of welded joints enhanced by ultrasonic peening treatment
| British Library Online Contents | 2011
Discussion on fatigue design of welded joints enhanced by ultrasonic peening treatment (UPT)
| British Library Online Contents | 2009
Investigation on Improving Fatigue Properties of Welded Joints by Ultrasonic Peening Method
| British Library Online Contents | 2000
The effects of ultrasonic peening treatment on the ultra-long life fatigue behavior of welded joints
| British Library Online Contents | 2010