The invention discloses a preparation method of a LAO (LaAlO3) doped composite YBCO film and belongs to the technical field of preparation of high-temperature superconducting materials. According to the method, organic La salt and Al salt are taken as precursor salts, a precursor solution is prepared with a chemical solution method and then applied to an LAO single crystal substrate with a spin coating method, and then a film is composited to the single crystal surface with a heating processing technology. According to the provided LAO doped composite film, the doping phase LAO can have a coherent boundary with YBCO, and the YBCO structure is not damaged while a pinning defect is introduced. An external solvent is not added, a system is simple, cost-saving, time for a sintering technology is shorter, and epitaxial growth of YBCO is not hindered while the LAO phase is formed. Je of a sample, doped with 5% of LAO, of the composite film under self-field is about 3 times of that of a pure YBCO film and is about 6 times of that of the pure YBCO film under an external field with 77 K and 1.5 T.
Preparation method of LAO (LaAlO3) doped composite YBCO film
The invention discloses a preparation method of a LAO (LaAlO3) doped composite YBCO film and belongs to the technical field of preparation of high-temperature superconducting materials. According to the method, organic La salt and Al salt are taken as precursor salts, a precursor solution is prepared with a chemical solution method and then applied to an LAO single crystal substrate with a spin coating method, and then a film is composited to the single crystal surface with a heating processing technology. According to the provided LAO doped composite film, the doping phase LAO can have a coherent boundary with YBCO, and the YBCO structure is not damaged while a pinning defect is introduced. An external solvent is not added, a system is simple, cost-saving, time for a sintering technology is shorter, and epitaxial growth of YBCO is not hindered while the LAO phase is formed. Je of a sample, doped with 5% of LAO, of the composite film under self-field is about 3 times of that of a pure YBCO film and is about 6 times of that of the pure YBCO film under an external field with 77 K and 1.5 T.
Preparation method of LAO (LaAlO3) doped composite YBCO film
SUO HONGLI (Autor:in) / XU YAN (Autor:in) / LIU MIN (Autor:in) / MA LIN (Autor:in) / YI NING (Autor:in)
27.01.2016
Patent
Elektronische Ressource
Englisch
| British Library Online Contents | 2004
Method for preparing double mismatch multi-element doped composite YBCO thin film
| Europäisches Patentamt | 2015
| British Library Online Contents | 2005
CaTiO3-LaAlO3-based microwave dielectric ceramic and preparation method thereof
| Europäisches Patentamt | 2024
Preparation method of YBCO film with high magnetic flux pinning performance
| Europäisches Patentamt | 2015