Microcrystalline glaze, wear-resistant glaze, transparent microcrystalline wear-resistant full-polished glaze ceramic tile and preparation method
The invention relates to transparent microcrystalline glaze, a wear-resistant transparent glaze, a transparent microcrystalline wear-resistant full-polished glaze ceramic tile and a preparation method. The transparent microcrystalline glaze comprises the following components in parts by weight: 5 parts of barium carbonate; 18 parts of potassium feldspar; 9 parts of albite; 8 parts of aluminum oxide; 16 parts of calcite; 4 parts of quartz powder; 6 parts of dolomite; 10 parts of kaolin; 12 parts of calcined kaolin; 5 parts of wollastonite; 1 part of calcium fluoride; 1 part of titanium dioxide.The preparation method of the transparent microcrystalline wear-resistant full-polished glazed ceramic tile comprises the following steps: (1) pressing a green body; (2) applying/not applying groundcoat; (3) drying or not drying a glaze line; (4) carrying out comprehensive combined decoration including planographic printing, rubber roller printing, ink jet printing and the like; (5) drying or not drying a glaze line; (6) applying transparent microcrystalline glaze; (7) pouring/spraying wear-resistant transparent glaze; (8) performing firing in a kiln; and (9) conducting glaze polishing.
本发明涉及透明微晶釉、耐磨透明釉、透明微晶耐磨全抛釉瓷砖及制备方法，透明微晶釉按重量份：烧氧化锌5份；碳酸钡5份；钾长石18份；钠长石9份；氧化铝8份；方解石16份；石英粉4份；白云石6份；高岭土10份；煅烧高岭土12份；硅灰石5份；氟化钙1份；钛白粉1份。透明微晶耐磨全抛釉瓷砖的制备方法，包括：⑴坯体压制；⑵施/不施底釉；⑶釉线干燥或不干燥：⑷进行包括平板、胶辊、喷墨等综合组合装饰；⑸釉线干燥或不干燥；⑹施透明微晶釉；⑺淋/喷耐磨透明釉；⑻入窑烧成；⑼釉面抛光。
Microcrystalline glaze, wear-resistant glaze, transparent microcrystalline wear-resistant full-polished glaze ceramic tile and preparation method
The invention relates to transparent microcrystalline glaze, a wear-resistant transparent glaze, a transparent microcrystalline wear-resistant full-polished glaze ceramic tile and a preparation method. The transparent microcrystalline glaze comprises the following components in parts by weight: 5 parts of barium carbonate; 18 parts of potassium feldspar; 9 parts of albite; 8 parts of aluminum oxide; 16 parts of calcite; 4 parts of quartz powder; 6 parts of dolomite; 10 parts of kaolin; 12 parts of calcined kaolin; 5 parts of wollastonite; 1 part of calcium fluoride; 1 part of titanium dioxide.The preparation method of the transparent microcrystalline wear-resistant full-polished glazed ceramic tile comprises the following steps: (1) pressing a green body; (2) applying/not applying groundcoat; (3) drying or not drying a glaze line; (4) carrying out comprehensive combined decoration including planographic printing, rubber roller printing, ink jet printing and the like; (5) drying or not drying a glaze line; (6) applying transparent microcrystalline glaze; (7) pouring/spraying wear-resistant transparent glaze; (8) performing firing in a kiln; and (9) conducting glaze polishing.
本发明涉及透明微晶釉、耐磨透明釉、透明微晶耐磨全抛釉瓷砖及制备方法，透明微晶釉按重量份：烧氧化锌5份；碳酸钡5份；钾长石18份；钠长石9份；氧化铝8份；方解石16份；石英粉4份；白云石6份；高岭土10份；煅烧高岭土12份；硅灰石5份；氟化钙1份；钛白粉1份。透明微晶耐磨全抛釉瓷砖的制备方法，包括：⑴坯体压制；⑵施/不施底釉；⑶釉线干燥或不干燥：⑷进行包括平板、胶辊、喷墨等综合组合装饰；⑸釉线干燥或不干燥；⑹施透明微晶釉；⑺淋/喷耐磨透明釉；⑻入窑烧成；⑼釉面抛光。
Microcrystalline glaze, wear-resistant glaze, transparent microcrystalline wear-resistant full-polished glaze ceramic tile and preparation method
微晶釉、耐磨釉、透明微晶耐磨全抛釉瓷砖及制备方法
XIAO HUIYIN (Autor:in) / WANG YONGQIANG (Autor:in) / SHEN RONGWEI (Autor:in) / LIU RENSONG (Autor:in) / GU ZHANWEN (Autor:in) / CHEN ZHICHUAN (Autor:in) / LI ZHENJIN (Autor:in)
18.08.2020
Patent
Elektronische Ressource
Chinesisch
| Europäisches Patentamt | 2024
| Europäisches Patentamt | 2022
| Europäisches Patentamt | 2024
| Europäisches Patentamt | 2021