Red ground coat of wood leaf cup and method for manufacturing wood leaf cup by adopting red ground coat of wood leaf cup
The invention discloses a red ground coat of a wood leaf cup and a method for manufacturing the wood leaf cup by adopting the red ground coat of the wood leaf cup. The red ground coat comprises glazeA and glaze B. The glaze B accounts for 10% of the weight of the glaze A. The glaze A is prepared from, by weight, 6%-8% of feldspar, 5%-6% of kaolin, 5%-6% of quartz, 5%-6% of chalk, 50%-60% of fritand 18% of pigment, and the sum of the percentages of all the raw materials is 100%. According to the red ground coat of the wood leaf cup and the method for manufacturing the wood leaf cup by adopting the red ground coat of the wood leaf cup, the color development intensity, stability, flowability and color development uniformity of the glaze are proper, the veins of leaves are clear, and the colors are gorgeous and glossy; the ground coat is free of heavy metal toxicity after being sintered at high temperature and can reach the food-grade standard; and the firing conditions are stable and reliable, the operability is high, the yield is high, the limitation that a traditional wood leaf cup adopts single black ground coat is broken through, and the development space of the wood leaf cup isexpanded.
本发明公开了一种木叶盏红色底釉及采用该木叶盏红色底釉制作木叶盏的方法，红色底釉包括釉料A和釉料B，所述釉料B占所述釉料A重量的10％，所述釉料A由如下原料制成：长石6％‑8％、高岭土5％‑6％、石英5％‑6％、白垩5％‑6％、熔块50％‑60％、色料18％，各原料的百分比之和为100％。该木叶盏红色底釉及采用该木叶盏红色底釉制作木叶盏的方法，釉料的发色强度、稳定性、流动性、发色均匀度适当，叶片脉络呈现清楚，色彩艳丽有光泽；底釉经高温烧成后无重金属毒性，可达食用级标准；烧制条件稳定可靠，可操作性强，成品率高，打破了传统木叶盏采用单一黑色底釉的局限，扩展了木叶盏的发展空间。
Red ground coat of wood leaf cup and method for manufacturing wood leaf cup by adopting red ground coat of wood leaf cup
The invention discloses a red ground coat of a wood leaf cup and a method for manufacturing the wood leaf cup by adopting the red ground coat of the wood leaf cup. The red ground coat comprises glazeA and glaze B. The glaze B accounts for 10% of the weight of the glaze A. The glaze A is prepared from, by weight, 6%-8% of feldspar, 5%-6% of kaolin, 5%-6% of quartz, 5%-6% of chalk, 50%-60% of fritand 18% of pigment, and the sum of the percentages of all the raw materials is 100%. According to the red ground coat of the wood leaf cup and the method for manufacturing the wood leaf cup by adopting the red ground coat of the wood leaf cup, the color development intensity, stability, flowability and color development uniformity of the glaze are proper, the veins of leaves are clear, and the colors are gorgeous and glossy; the ground coat is free of heavy metal toxicity after being sintered at high temperature and can reach the food-grade standard; and the firing conditions are stable and reliable, the operability is high, the yield is high, the limitation that a traditional wood leaf cup adopts single black ground coat is broken through, and the development space of the wood leaf cup isexpanded.
本发明公开了一种木叶盏红色底釉及采用该木叶盏红色底釉制作木叶盏的方法，红色底釉包括釉料A和釉料B，所述釉料B占所述釉料A重量的10％，所述釉料A由如下原料制成：长石6％‑8％、高岭土5％‑6％、石英5％‑6％、白垩5％‑6％、熔块50％‑60％、色料18％，各原料的百分比之和为100％。该木叶盏红色底釉及采用该木叶盏红色底釉制作木叶盏的方法，釉料的发色强度、稳定性、流动性、发色均匀度适当，叶片脉络呈现清楚，色彩艳丽有光泽；底釉经高温烧成后无重金属毒性，可达食用级标准；烧制条件稳定可靠，可操作性强，成品率高，打破了传统木叶盏采用单一黑色底釉的局限，扩展了木叶盏的发展空间。
Red ground coat of wood leaf cup and method for manufacturing wood leaf cup by adopting red ground coat of wood leaf cup
一种木叶盏红色底釉及采用该木叶盏红色底釉制作木叶盏的方法
FENG SHANXIN (Autor:in)
21.08.2020
Patent
Elektronische Ressource
Chinesisch
IPC:
C03C
Chemische Zusammensetzungen für Gläser, Glasuren oder Emails
,
CHEMICAL COMPOSITION OF GLASSES, GLAZES, OR VITREOUS ENAMELS
/
B28B
Formgeben von Ton oder anderen keramischen Stoffzusammensetzungen, Schlacke oder von Mischungen, die zementartiges Material enthalten, z.B. Putzmörtel
,
SHAPING CLAY OR OTHER CERAMIC COMPOSITIONS, SLAG OR MIXTURES CONTAINING CEMENTITIOUS MATERIAL, e.g. PLASTER
/
C04B
Kalk
,
LIME
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2020
Wood door leaf component, wood door leaf and manufacturing method of wood door leaf
| Europäisches Patentamt | 2015
Wood fiber door leaf and manufacturing process thereof
| Europäisches Patentamt | 2021