The invention relates to a blank for a crackle glaze ceramic product, wherein the blank comprises the components in parts by weight: (1) 12-20 parts of feldspar powder, (2) 50-80 parts of water-washedsoil, (3) 1-5 parts of talcum powder, (4) 8-18 parts of pyrophyllite, (5) 2-6 parts of clay and (6) 5-10 parts of frit. The preparation method comprises the steps: proportioning the materials, ballsand water according to a mass ratio of 1:1.5:(1.1-1.2), carrying out ball milling for 24 hours, adding water to dilute to 50-60 baume degrees when the fineness of the slurry reaches 0.4-0.6% of the screen residue of a 120-mesh sieve, and thus obtaining the slurry. The method is energy-saving, and the crack effect of the finished product is good.
本发明涉及一种裂纹釉陶瓷制品用坯料，按照重量份数计，它包括（1）长石粉12‑20份，（2）水洗土50‑80份，（3）滑石粉1‑5份，（4）叶蜡石8‑18份，（5）粘土2‑6份，（6）熔块5‑10份；其制备方法，它包括将料：球：水按照质量比1：1.5：1.1‑1.2配比，球磨24小时，当泥浆细度达到120目筛筛余为0.4‑0.6%即可，加水稀释至50‑60波美度制得泥浆。本发明节能，成品裂纹效果好。
The invention relates to a blank for a crackle glaze ceramic product, wherein the blank comprises the components in parts by weight: (1) 12-20 parts of feldspar powder, (2) 50-80 parts of water-washedsoil, (3) 1-5 parts of talcum powder, (4) 8-18 parts of pyrophyllite, (5) 2-6 parts of clay and (6) 5-10 parts of frit. The preparation method comprises the steps: proportioning the materials, ballsand water according to a mass ratio of 1:1.5:(1.1-1.2), carrying out ball milling for 24 hours, adding water to dilute to 50-60 baume degrees when the fineness of the slurry reaches 0.4-0.6% of the screen residue of a 120-mesh sieve, and thus obtaining the slurry. The method is energy-saving, and the crack effect of the finished product is good.
本发明涉及一种裂纹釉陶瓷制品用坯料，按照重量份数计，它包括（1）长石粉12‑20份，（2）水洗土50‑80份，（3）滑石粉1‑5份，（4）叶蜡石8‑18份，（5）粘土2‑6份，（6）熔块5‑10份；其制备方法，它包括将料：球：水按照质量比1：1.5：1.1‑1.2配比，球磨24小时，当泥浆细度达到120目筛筛余为0.4‑0.6%即可，加水稀释至50‑60波美度制得泥浆。本发明节能，成品裂纹效果好。
Blank for crackle glaze ceramic product
一种裂纹釉陶瓷制品用坯料
YANG QINGHUA (Autor:in)
22.09.2020
Patent
Elektronische Ressource
Chinesisch
Crackle glaze based on perlite
| Engineering Index Backfile | 1965
High-strength medium-temperature crackle glaze ceramic product and manufacturing method thereof
| Europäisches Patentamt | 2021
Manufacturing method of high-strength crackle glaze ceramic wine bottle
| Europäisches Patentamt | 2021