Dehua Jianbai porcelain and preparation method thereof
The invention discloses Dehua Jianbai porcelain and a preparation method thereof. A Jianbai porcelain blank is prepared from the following raw materials in parts by weight: 50-60 parts of Dehua kaolin, 6-12 parts of sand grains, 6-9 parts of Dehua feldspar, 5-10 parts of calcined black talc, 3-8 parts of diopside, 6-10 parts of quartzite and 1-4 parts of clay. According to the Dehua Jianbai porcelain, sand grains which are low in price and rich in source are selected to replace raw materials such as nano silicon dioxide, the use of a binder is reduced, the utilization rate of resources is increased, and the cost can be saved; and meanwhile, Dehua kaolin is selected, the firing temperature can be reduced, the firing period is shortened, the process energy consumption is reduced, the cost isfurther reduced, and the economic value is improved.
本发明公开了一种德化建白瓷及其制备方法，所述建白瓷坯体由以下重量份的原料制备而成：德化高岭土50份～60份、沙粒6份～12份、德化长石6份～9份、煅烧黑滑石5份～10份、透辉石3份～8份、石英石6份～10份、黏土1份～4份。本发明德化建白瓷，选用价格低廉、来源丰富的沙粒代替纳米二氧化硅等原料，减少粘结剂的使用，增加资源的利用率，又可以节约成本，同时选用德化高岭土，可降低烧成温度，缩短烧成周期，减少工艺能耗，进一步降低成本，提高了经济价值。
Dehua Jianbai porcelain and preparation method thereof
The invention discloses Dehua Jianbai porcelain and a preparation method thereof. A Jianbai porcelain blank is prepared from the following raw materials in parts by weight: 50-60 parts of Dehua kaolin, 6-12 parts of sand grains, 6-9 parts of Dehua feldspar, 5-10 parts of calcined black talc, 3-8 parts of diopside, 6-10 parts of quartzite and 1-4 parts of clay. According to the Dehua Jianbai porcelain, sand grains which are low in price and rich in source are selected to replace raw materials such as nano silicon dioxide, the use of a binder is reduced, the utilization rate of resources is increased, and the cost can be saved; and meanwhile, Dehua kaolin is selected, the firing temperature can be reduced, the firing period is shortened, the process energy consumption is reduced, the cost isfurther reduced, and the economic value is improved.
本发明公开了一种德化建白瓷及其制备方法，所述建白瓷坯体由以下重量份的原料制备而成：德化高岭土50份～60份、沙粒6份～12份、德化长石6份～9份、煅烧黑滑石5份～10份、透辉石3份～8份、石英石6份～10份、黏土1份～4份。本发明德化建白瓷，选用价格低廉、来源丰富的沙粒代替纳米二氧化硅等原料，减少粘结剂的使用，增加资源的利用率，又可以节约成本，同时选用德化高岭土，可降低烧成温度，缩短烧成周期，减少工艺能耗，进一步降低成本，提高了经济价值。
Dehua Jianbai porcelain and preparation method thereof
一种德化建白瓷及其制备方法
ZENG GUOBIN (Autor:in)
27.11.2020
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Porcelain clay, and porcelain and preparation method thereof
| Europäisches Patentamt | 2021
Alumina-based porcelain insulator porcelain body and preparation method thereof
| Europäisches Patentamt | 2024
Jun porcelain celeste blue glazed porcelain and preparation method thereof
| Europäisches Patentamt | 2021