High-strength light yellow-green glaze and method for preparing ceramic product by using same
The invention discloses a high-strength light yellow-green glaze and a method for preparing a ceramic product by using the same, belonging to the technical field of ceramics. The high-strength light yellow-green glaze comprises the following components in parts by mass: 40 to 50 parts of feldspar powder, 20 to 25 parts of quartz, 20 to 24 parts of calcite, 15 to 20 parts of albite, 5 to 8 parts ofkaolin, 5 to 10 parts of talcum powder, 5 to 7 parts of barium carbonate, 5 to 10 parts of zirconium frit, 6 to 11 parts of zirconium silicate and 5 to 7 parts of dolomite. The method for preparing the ceramic product by using the glaze comprises the following steps: ball-milling and sieving, preparation of glaze slip, glazing, and firing.
本发明公开了一种高强度浅黄绿色釉料及用其制备陶瓷制品的方法，属于陶瓷技术领域。本发明的高强度浅黄绿色釉料，包括按照质量份数计的如下组份：长石粉40~50份，石英20~25份，方解石20~24份，钠长石15~20份，高岭土5~8份，滑石粉5~10份，碳酸钡5~7份，锆熔块5~10份，硅酸锆6~11份，白云石5~7份。用其制备陶瓷制品的方法，包括如下步骤：球磨及过筛、制备釉浆、施釉及烧制。
High-strength light yellow-green glaze and method for preparing ceramic product by using same
The invention discloses a high-strength light yellow-green glaze and a method for preparing a ceramic product by using the same, belonging to the technical field of ceramics. The high-strength light yellow-green glaze comprises the following components in parts by mass: 40 to 50 parts of feldspar powder, 20 to 25 parts of quartz, 20 to 24 parts of calcite, 15 to 20 parts of albite, 5 to 8 parts ofkaolin, 5 to 10 parts of talcum powder, 5 to 7 parts of barium carbonate, 5 to 10 parts of zirconium frit, 6 to 11 parts of zirconium silicate and 5 to 7 parts of dolomite. The method for preparing the ceramic product by using the glaze comprises the following steps: ball-milling and sieving, preparation of glaze slip, glazing, and firing.
本发明公开了一种高强度浅黄绿色釉料及用其制备陶瓷制品的方法，属于陶瓷技术领域。本发明的高强度浅黄绿色釉料，包括按照质量份数计的如下组份：长石粉40~50份，石英20~25份，方解石20~24份，钠长石15~20份，高岭土5~8份，滑石粉5~10份，碳酸钡5~7份，锆熔块5~10份，硅酸锆6~11份，白云石5~7份。用其制备陶瓷制品的方法，包括如下步骤：球磨及过筛、制备釉浆、施釉及烧制。
High-strength light yellow-green glaze and method for preparing ceramic product by using same
高强度浅黄绿色釉料及用其制备陶瓷制品的方法
XU ZHENSHUANG (Autor:in)
01.12.2020
Patent
Elektronische Ressource
Chinesisch
Method for preparing water soluble yellow ceramic glaze
| Europäisches Patentamt | 2015
| Europäisches Patentamt | 2023
Ceramic glaze and method for preparing ceramic product by using same
| Europäisches Patentamt | 2024
Cream glaze and method for preparing cream glaze ceramic product by using cream glaze
| Europäisches Patentamt | 2021
| Europäisches Patentamt | 2015