Fireproof material for preparing fireproof profile and method for preparing fireproof profile
The invention discloses a fireproof material for preparing a fireproof profile and a method for preparing the fireproof profile. The fireproof material comprises magnesium oxysulfate cement, expandedperlite, fireproof fibers, vermiculite, a cement reinforcing agent and fireproof glue, wherein the weight percentage ratio of the magnesium oxysulfate cement to the expanded perlite is 1:(0.001-0.01),the weight percentage ratio of the magnesium oxysulfate cement to the fireproof fibers is 1:(0.01-0.1), the weight percentage ratio of the magnesium oxysulfate cement to the vermiculite is 1:(0.001-0.1), the weight percentage ratio of the magnesium oxysulfate cement to the cement reinforcing agent is 1:(0.005-0.1), and the weight percentage ratio of the magnesium oxysulfate cement to the fireproof glue is 1:(0.001-0.1). The fireproof material provided by the invention has meshes, the prepared fireproof material is light, and the fireproof material has the characteristics of fire resistance, water resistance, sound insulation, heat insulation, high-temperature resistance and the like, does not deform, explode or scratch under 1500 DEG C big fire barbecue, and does not leak water or air at-50 DEG C.
本发明公开一种用于制备防火型材的防火材料及其制备防火型材方法，包括硫氧镁水泥、膨胀珍珠岩、防火纤维、蛭石、水泥增强剂和防火胶；其中，硫氧镁水泥与膨胀珍珠岩的重量百分比为1∶（0.001～0.01），硫氧镁水泥与防火纤维的重量百分比为1∶（0.01～0.1），硫氧镁水泥与蛭石的重量百分比为1∶（0.001～0.1），硫氧镁水泥与水泥增强剂的重量百分比为1∶（0.005～0.1），硫氧镁水泥与防火胶的重量百分比为1∶（0.001～0.1）本发明的防火材料具有网孔，制备的防火型材质轻，本发明的防火材料有防火，防水，隔音，隔热，防高温等特点，在1500℃大火烧烤下不变型，不炸裂，无伤痕，在零下50度下不漏水不漏风。
Fireproof material for preparing fireproof profile and method for preparing fireproof profile
The invention discloses a fireproof material for preparing a fireproof profile and a method for preparing the fireproof profile. The fireproof material comprises magnesium oxysulfate cement, expandedperlite, fireproof fibers, vermiculite, a cement reinforcing agent and fireproof glue, wherein the weight percentage ratio of the magnesium oxysulfate cement to the expanded perlite is 1:(0.001-0.01),the weight percentage ratio of the magnesium oxysulfate cement to the fireproof fibers is 1:(0.01-0.1), the weight percentage ratio of the magnesium oxysulfate cement to the vermiculite is 1:(0.001-0.1), the weight percentage ratio of the magnesium oxysulfate cement to the cement reinforcing agent is 1:(0.005-0.1), and the weight percentage ratio of the magnesium oxysulfate cement to the fireproof glue is 1:(0.001-0.1). The fireproof material provided by the invention has meshes, the prepared fireproof material is light, and the fireproof material has the characteristics of fire resistance, water resistance, sound insulation, heat insulation, high-temperature resistance and the like, does not deform, explode or scratch under 1500 DEG C big fire barbecue, and does not leak water or air at-50 DEG C.
本发明公开一种用于制备防火型材的防火材料及其制备防火型材方法，包括硫氧镁水泥、膨胀珍珠岩、防火纤维、蛭石、水泥增强剂和防火胶；其中，硫氧镁水泥与膨胀珍珠岩的重量百分比为1∶（0.001～0.01），硫氧镁水泥与防火纤维的重量百分比为1∶（0.01～0.1），硫氧镁水泥与蛭石的重量百分比为1∶（0.001～0.1），硫氧镁水泥与水泥增强剂的重量百分比为1∶（0.005～0.1），硫氧镁水泥与防火胶的重量百分比为1∶（0.001～0.1）本发明的防火材料具有网孔，制备的防火型材质轻，本发明的防火材料有防火，防水，隔音，隔热，防高温等特点，在1500℃大火烧烤下不变型，不炸裂，无伤痕，在零下50度下不漏水不漏风。
Fireproof material for preparing fireproof profile and method for preparing fireproof profile
一种用于制备防火型材的防火材料及其制备防火型材方法
GAO JINGJING (Autor:in)
11.12.2020
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Fireproof door and preparing method of fireproof door
| Europäisches Patentamt | 2015
Fireproof material impregnation liquid and method for preparing fireproof insulation board
| Europäisches Patentamt | 2020
Fireproof profile, fireproof joint assembly, and method for assembling a fireproof joint assembly
| Europäisches Patentamt | 2020
FIREPROOF PROFILE, FIREPROOF JOINT ASSEMBLY, AND METHOD FOR ASSEMBLING A FIREPROOF JOINT ASSEMBLY
| Europäisches Patentamt | 2019