Wear-resistant and anti-fouling glaze as well as preparation method and application thereof
The invention discloses a wear-resistant anti-fouling glaze. The glaze is prepared from the following raw materials: potassium feldspar, albite, quartz, kaolin, oxide and talc according to a mass ratio of 23-28: 20-25: 35-45: 3-6: 3-6: 2-4. After the wear-resistant and anti-fouling glaze is applied to an electric porcelain blank and is put into a kiln to be fired, the glaze has few pinholes and excellent wear resistance, anti-fouling performance and high temperature resistance, and meanwhile, the glossiness of the glaze can be improved; the situation that the electric porcelain glaze layer isprone to abrasion under the severe environment of heavy sandstorm is avoided, the electric porcelain product with the electric porcelain glaze layer is resistant to high pressure, and safe operation of an electric power system is guaranteed.
本发明公开了一种耐磨、防污釉料，该釉料所用原料及其重量比为：钾长石∶钠长石∶石英∶高岭土∶氧化∶滑石＝23‑28∶20‑25∶35‑45∶3‑6∶3‑6∶2‑4。所述的耐磨、防污釉料施加于电瓷坯体上并入窑烧制后，釉面针孔少，耐磨、防污、耐高温性能优异，同时釉面的光泽度能够得到提高；避免了在大风沙的恶劣环境下，电瓷釉层容易出现磨损的情况发生，并且应用本发明的电瓷产品耐高压，确保了电力系统的安全运行。
Wear-resistant and anti-fouling glaze as well as preparation method and application thereof
The invention discloses a wear-resistant anti-fouling glaze. The glaze is prepared from the following raw materials: potassium feldspar, albite, quartz, kaolin, oxide and talc according to a mass ratio of 23-28: 20-25: 35-45: 3-6: 3-6: 2-4. After the wear-resistant and anti-fouling glaze is applied to an electric porcelain blank and is put into a kiln to be fired, the glaze has few pinholes and excellent wear resistance, anti-fouling performance and high temperature resistance, and meanwhile, the glossiness of the glaze can be improved; the situation that the electric porcelain glaze layer isprone to abrasion under the severe environment of heavy sandstorm is avoided, the electric porcelain product with the electric porcelain glaze layer is resistant to high pressure, and safe operation of an electric power system is guaranteed.
本发明公开了一种耐磨、防污釉料，该釉料所用原料及其重量比为：钾长石∶钠长石∶石英∶高岭土∶氧化∶滑石＝23‑28∶20‑25∶35‑45∶3‑6∶3‑6∶2‑4。所述的耐磨、防污釉料施加于电瓷坯体上并入窑烧制后，釉面针孔少，耐磨、防污、耐高温性能优异，同时釉面的光泽度能够得到提高；避免了在大风沙的恶劣环境下，电瓷釉层容易出现磨损的情况发生，并且应用本发明的电瓷产品耐高压，确保了电力系统的安全运行。
Wear-resistant and anti-fouling glaze as well as preparation method and application thereof
一种耐磨、防污釉料及其制备方法和应用
LIU YINGYING (Autor:in) / LIU JUNRONG (Autor:in)
29.12.2020
Patent
Elektronische Ressource
Chinesisch
| Europäisches Patentamt | 2023
Antibacterial wear-resistant glaze and preparation method thereof
| Europäisches Patentamt | 2021
Preparation method of wear-resistant glaze daily porcelain glaze
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2020