Tang-fancy glaze current firing glaze material and method for preparing porcelain by adopting Tang-fancy glaze current firing glaze material
The invention belongs to the technical field of glaze preparation, and particularly relates to a Tang-fancy glaze current firing glaze which is prepared from the following raw materials in parts by weight: 30-45 parts of white feldspar, 18-30 parts of calcite, 7-12 parts of quartz, 1-2 parts of titanium oxide, 8-12 parts of frit, 5-10 parts of talc, 1-3 parts of zinc oxide and 1-2 parts of bone meal. The invention also discloses a method for preparing porcelain by using the Tang-fancy glaze current firing glaze. The method comprises the following steps: weighing various raw materials accordingto a certain proportion, fully crushing the raw materials, uniformly mixing, adding the mixed glaze into a ball mill, adding water, carrying out ball milling to obtain glaze slip, and finally uniformly applying the glaze slip to a biscuit firing blank, drying, and firing in a kiln to obtain Tang-fancy glaze current fired porcelain; on the basis of the Tangdong fancy glaze porcelain, improvement and creation are carried out by utilizing modern technologies at present, clustering and blending of blue, red, cyan and the like are realized on the basis of classic basic tones of black, white, yellow and the like, and the artistic effects of dark black in blue, alternate blue and white, blending of five colors and colorful glaze colors are realized.
本发明属于釉料制备技术领域，具体涉及一种唐花釉今烧釉料，它是由以下重量份的原料制备而成：白长石30‑45份，方解石18‑30份，石英7‑12份，氧化钛1‑2份，熔块8‑12份，滑石5‑10份，氧化锌1‑3份，骨粉1‑2份；本发明还公开了采用唐花釉今烧釉料制备瓷器的方法，包括以下步骤：按一定比例称取各种原料，并将原料充分粉碎后混匀，之后将混合釉料加入球磨机中，加水球磨得到釉浆，最后将釉浆均匀地施敷在素烧坯上，干燥后放入窑炉中烧制得到唐花釉今烧瓷器；本发明在唐代花釉瓷器的基础上，利用今天的现代化技术加以改良创造，在经典的黑、白、黄等基础色调上，实现蓝、红、青等簇拥和交融，实现蓝中隐黑、蓝白相间，再到五彩交融、釉色纷呈的艺术效果。
Tang-fancy glaze current firing glaze material and method for preparing porcelain by adopting Tang-fancy glaze current firing glaze material
The invention belongs to the technical field of glaze preparation, and particularly relates to a Tang-fancy glaze current firing glaze which is prepared from the following raw materials in parts by weight: 30-45 parts of white feldspar, 18-30 parts of calcite, 7-12 parts of quartz, 1-2 parts of titanium oxide, 8-12 parts of frit, 5-10 parts of talc, 1-3 parts of zinc oxide and 1-2 parts of bone meal. The invention also discloses a method for preparing porcelain by using the Tang-fancy glaze current firing glaze. The method comprises the following steps: weighing various raw materials accordingto a certain proportion, fully crushing the raw materials, uniformly mixing, adding the mixed glaze into a ball mill, adding water, carrying out ball milling to obtain glaze slip, and finally uniformly applying the glaze slip to a biscuit firing blank, drying, and firing in a kiln to obtain Tang-fancy glaze current fired porcelain; on the basis of the Tangdong fancy glaze porcelain, improvement and creation are carried out by utilizing modern technologies at present, clustering and blending of blue, red, cyan and the like are realized on the basis of classic basic tones of black, white, yellow and the like, and the artistic effects of dark black in blue, alternate blue and white, blending of five colors and colorful glaze colors are realized.
本发明属于釉料制备技术领域，具体涉及一种唐花釉今烧釉料，它是由以下重量份的原料制备而成：白长石30‑45份，方解石18‑30份，石英7‑12份，氧化钛1‑2份，熔块8‑12份，滑石5‑10份，氧化锌1‑3份，骨粉1‑2份；本发明还公开了采用唐花釉今烧釉料制备瓷器的方法，包括以下步骤：按一定比例称取各种原料，并将原料充分粉碎后混匀，之后将混合釉料加入球磨机中，加水球磨得到釉浆，最后将釉浆均匀地施敷在素烧坯上，干燥后放入窑炉中烧制得到唐花釉今烧瓷器；本发明在唐代花釉瓷器的基础上，利用今天的现代化技术加以改良创造，在经典的黑、白、黄等基础色调上，实现蓝、红、青等簇拥和交融，实现蓝中隐黑、蓝白相间，再到五彩交融、釉色纷呈的艺术效果。
Tang-fancy glaze current firing glaze material and method for preparing porcelain by adopting Tang-fancy glaze current firing glaze material
一种唐花釉今烧釉料及采用该唐花釉今烧釉料制备瓷器的方法
ZHANG GUANJUN (Autor:in) / BIAN JIWEI (Autor:in) / ZHANG PEILIN (Autor:in)
29.01.2021
Patent
Elektronische Ressource
Chinesisch
Glaze spraying system, fancy glaze eggshell porcelain and preparation method thereof
| Europäisches Patentamt | 2020
Yunxia fancy glaze and oxidation firing method thereof
| Europäisches Patentamt | 2022
| Europäisches Patentamt | 2024
Song dynasty jun fancy glaze and reduction firing method thereof
| Europäisches Patentamt | 2022
Glaze material for firing Longquan celadon thick glaze and firing process
| Europäisches Patentamt | 2022