Song dynasty jun fancy glaze and reduction firing method thereof
The invention relates to the technical field of ceramic production, and discloses a Song dynasty Jun fancy glaze formula, which comprises 20-65 parts of potassium feldspar, 12-18 parts of calcite, 3-9 parts of lithium fluoride, 3-11 parts of talcum powder, 6-10 parts of Benyuan, 8-16 parts of barium carbonate, 6-16 parts of quartz, and 2-8 parts of nano platinum powder. The invention also provides a reduction firing method of the Song dynasty Jun fancy glaze, which comprises the following steps: S1, ball milling: weighing the raw materials in the formula, and then respectively carrying out ball milling in a wet ball milling manner; s2, stirring and mixing: putting the raw materials of the mixed material A into a stirrer, and stirring and mixing to obtain the mixed material A; the Jun porcelain glaze is reasonable in compatibility, natural raw materials are matched with one another, the prepared Jun porcelain glaze has stereoscopic impression, good fluidity, good gloss and good glazing color glossiness and transparency, organic matter in the glaze is oxidized and volatilized through distributed firing, a blank can be porcelainized through high-temperature reduction, the strength is improved, and meanwhile the glaze color is brighter.
本发明涉及陶瓷生产技术领域，且公开了宋钧花釉配方，配方包括：钾长石20‑65份，方解石12‑18份、氟化锂3‑9份、滑石粉3‑11份、本石岳6‑10份，碳酸钡8‑16份、石英6‑16份、纳米铂粉2‑8份；本发明还提出了宋钧花釉还原烧制方法，包括以下步骤：S1：球磨，称取配方中的原料，然后用湿法球磨的方式分别进行球磨；S2：搅拌混合，把混合物料A的原料放入搅拌机中进行搅拌混合，得到混合物料A。本发明配伍合理，自然原料相互配合，制作的钧瓷釉料有立体感，流动性好，光泽好，釉色的光泽度和透明度好，分布烧制使得釉料中的有机物进行氧化挥发，通过高温还原能够使得坯胎瓷化，提高强度，同时使得釉面色彩更加鲜艳。
Song dynasty jun fancy glaze and reduction firing method thereof
The invention relates to the technical field of ceramic production, and discloses a Song dynasty Jun fancy glaze formula, which comprises 20-65 parts of potassium feldspar, 12-18 parts of calcite, 3-9 parts of lithium fluoride, 3-11 parts of talcum powder, 6-10 parts of Benyuan, 8-16 parts of barium carbonate, 6-16 parts of quartz, and 2-8 parts of nano platinum powder. The invention also provides a reduction firing method of the Song dynasty Jun fancy glaze, which comprises the following steps: S1, ball milling: weighing the raw materials in the formula, and then respectively carrying out ball milling in a wet ball milling manner; s2, stirring and mixing: putting the raw materials of the mixed material A into a stirrer, and stirring and mixing to obtain the mixed material A; the Jun porcelain glaze is reasonable in compatibility, natural raw materials are matched with one another, the prepared Jun porcelain glaze has stereoscopic impression, good fluidity, good gloss and good glazing color glossiness and transparency, organic matter in the glaze is oxidized and volatilized through distributed firing, a blank can be porcelainized through high-temperature reduction, the strength is improved, and meanwhile the glaze color is brighter.
本发明涉及陶瓷生产技术领域，且公开了宋钧花釉配方，配方包括：钾长石20‑65份，方解石12‑18份、氟化锂3‑9份、滑石粉3‑11份、本石岳6‑10份，碳酸钡8‑16份、石英6‑16份、纳米铂粉2‑8份；本发明还提出了宋钧花釉还原烧制方法，包括以下步骤：S1：球磨，称取配方中的原料，然后用湿法球磨的方式分别进行球磨；S2：搅拌混合，把混合物料A的原料放入搅拌机中进行搅拌混合，得到混合物料A。本发明配伍合理，自然原料相互配合，制作的钧瓷釉料有立体感，流动性好，光泽好，釉色的光泽度和透明度好，分布烧制使得釉料中的有机物进行氧化挥发，通过高温还原能够使得坯胎瓷化，提高强度，同时使得釉面色彩更加鲜艳。
Song dynasty jun fancy glaze and reduction firing method thereof
宋钧花釉及其还原烧制方法
WEI LIANJIN (Autor:in)
15.03.2022
Patent
Elektronische Ressource
Chinesisch
Yunxia fancy glaze and oxidation firing method thereof
| Europäisches Patentamt | 2022
| Europäisches Patentamt | 2021
Glaze spraying system, fancy glaze eggshell porcelain and preparation method thereof
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2024
| Europäisches Patentamt | 2024