Method for manufacturing high-grade building materials of landscape bricks and archaized bricks from coal gangue
The invention relates to a method for manufacturing a high-grade building materials of landscape bricks and archaized bricks from coal gangue, which comprises the following steps of: finely grinding the coal gangue to pass through a 0.42 mm sieve, finely grinding bentonite to pass through a 0.18 mm sieve, and fully and uniformly mixing and stirring the sieved coal gangue and bentonite to obtain a mixed material; putting sodium hexametaphosphate and hydroxymethyl cellulose into water to be diluted, uniformly spraying on the surface of the mixed material, and uniformly stirring the materials ; after aging, putting into a forming mold, and pressing by using a 350-ton hydraulic machine to obtain a semi-finished blank; and drying the semi-finished green body for 24 hours in an environment with the temperature of 42 DEG C and the relative humidity of 70%, putting the dried semi-finished green body into a tunnel kiln, carrying out gradient heating roasting, cooling in a reducing atmosphere, and discharging the cooled semi-finished green body out of the tunnel kiln to obtain the landscape brick. The high-grade building material for the landscape bricks and the archaized bricks takes the coal gangue as a main raw material, is environment-friendly and economical, has the characteristic of high strength, is high in product yield, and is a high-grade building material for the landscape bricks and the archaized bricks with high ornamental value and practicability.
一种利用煤矸石制作景观砖、仿古砖高档建筑材料的方法，取煤矸石磨细过0.42mm筛全通过，取斑脱石磨细过0.18mm筛全通过，把过筛后的煤矸石和斑脱石充分混拌均匀，得到混合物料；取六偏磷酸钠、取羟甲基纤维素放入水中稀释均匀喷洒在混合物料表面，搅拌均匀；陈化后，放入成型模具中，用350吨液压机压制，获得半成品坯体；将半成品坯体在温度42℃、相对湿度70％的环境中，烘干24h后，装入隧道窑中，梯度升温焙烧后，在还原气氛下冷却，出窑，得到景观砖。该景观砖、仿古砖高档建筑材料以煤矸石为主要原料，环保、经济，制作的建筑材料具有高强度的特点，产品成品率高，是一种高观赏性和实用性的优质景观砖、仿古砖高档建材。
Method for manufacturing high-grade building materials of landscape bricks and archaized bricks from coal gangue
The invention relates to a method for manufacturing a high-grade building materials of landscape bricks and archaized bricks from coal gangue, which comprises the following steps of: finely grinding the coal gangue to pass through a 0.42 mm sieve, finely grinding bentonite to pass through a 0.18 mm sieve, and fully and uniformly mixing and stirring the sieved coal gangue and bentonite to obtain a mixed material; putting sodium hexametaphosphate and hydroxymethyl cellulose into water to be diluted, uniformly spraying on the surface of the mixed material, and uniformly stirring the materials ; after aging, putting into a forming mold, and pressing by using a 350-ton hydraulic machine to obtain a semi-finished blank; and drying the semi-finished green body for 24 hours in an environment with the temperature of 42 DEG C and the relative humidity of 70%, putting the dried semi-finished green body into a tunnel kiln, carrying out gradient heating roasting, cooling in a reducing atmosphere, and discharging the cooled semi-finished green body out of the tunnel kiln to obtain the landscape brick. The high-grade building material for the landscape bricks and the archaized bricks takes the coal gangue as a main raw material, is environment-friendly and economical, has the characteristic of high strength, is high in product yield, and is a high-grade building material for the landscape bricks and the archaized bricks with high ornamental value and practicability.
一种利用煤矸石制作景观砖、仿古砖高档建筑材料的方法，取煤矸石磨细过0.42mm筛全通过，取斑脱石磨细过0.18mm筛全通过，把过筛后的煤矸石和斑脱石充分混拌均匀，得到混合物料；取六偏磷酸钠、取羟甲基纤维素放入水中稀释均匀喷洒在混合物料表面，搅拌均匀；陈化后，放入成型模具中，用350吨液压机压制，获得半成品坯体；将半成品坯体在温度42℃、相对湿度70％的环境中，烘干24h后，装入隧道窑中，梯度升温焙烧后，在还原气氛下冷却，出窑，得到景观砖。该景观砖、仿古砖高档建筑材料以煤矸石为主要原料，环保、经济，制作的建筑材料具有高强度的特点，产品成品率高，是一种高观赏性和实用性的优质景观砖、仿古砖高档建材。
Method for manufacturing high-grade building materials of landscape bricks and archaized bricks from coal gangue
利用煤矸石制作景观砖、仿古砖高档建筑材料的方法
QU ZHENSHI (Autor:in) / LI MINGZHEN (Autor:in) / PANG AIXUE (Autor:in)
02.07.2021
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Preparation method of twisted pottery archaized bricks
| Europäisches Patentamt | 2015
Preparation method of coal gangue archaized black brick
| Europäisches Patentamt | 2020
Method for producing double-specification archaized bricks sintered in same kiln
| Europäisches Patentamt | 2016