Corrosion-resistant glaze for pottery pot and glazing method thereof
The invention discloses a corrosion-resistant glaze material for a pottery pot. The corrosion-resistant glaze is prepared from the following raw materials in parts by weight: 20 to 50 parts of kaolin, 5 to 20 parts of limestone, 7 to 21 parts of potassium feldspar, 8 to 24 parts of lepidolite, 1 to 5 parts of zirconium oxide, 2.6 to 3.4 parts of zinc oxide, 1.3 to 2.7 parts of tin oxide, 10 to 20 parts of terpene resin and 15 to 30 parts of 1-hydroxyethylidene-1, 1-diphosphonate. The invention further discloses a glazing method of the corrosion-resistant glaze for the pottery pot, the process is simple, and raw materials are easy to obtain. The pottery pot glaze prepared by the method has the characteristic of excellent corrosion resistance.
本发明公开了一种陶罐的耐腐蚀釉料，包括以下按重量份数配比的原料：高岭土20‑50份，石灰石5‑20份，钾长石7‑21份，锂云母8‑24份，氧化锆1‑5份，氧化锌2.6‑3.4份，氧化锡1.3‑2.7份，萜烯树脂10‑20份，羟基乙叉二膦酸盐15‑30份。本发明还公开了一种陶罐的耐腐蚀釉料的施釉方法，工艺简单，原料易得。本发明制备所得的陶罐釉面具有耐腐蚀性能优异的特点。
Corrosion-resistant glaze for pottery pot and glazing method thereof
The invention discloses a corrosion-resistant glaze material for a pottery pot. The corrosion-resistant glaze is prepared from the following raw materials in parts by weight: 20 to 50 parts of kaolin, 5 to 20 parts of limestone, 7 to 21 parts of potassium feldspar, 8 to 24 parts of lepidolite, 1 to 5 parts of zirconium oxide, 2.6 to 3.4 parts of zinc oxide, 1.3 to 2.7 parts of tin oxide, 10 to 20 parts of terpene resin and 15 to 30 parts of 1-hydroxyethylidene-1, 1-diphosphonate. The invention further discloses a glazing method of the corrosion-resistant glaze for the pottery pot, the process is simple, and raw materials are easy to obtain. The pottery pot glaze prepared by the method has the characteristic of excellent corrosion resistance.
本发明公开了一种陶罐的耐腐蚀釉料，包括以下按重量份数配比的原料：高岭土20‑50份，石灰石5‑20份，钾长石7‑21份，锂云母8‑24份，氧化锆1‑5份，氧化锌2.6‑3.4份，氧化锡1.3‑2.7份，萜烯树脂10‑20份，羟基乙叉二膦酸盐15‑30份。本发明还公开了一种陶罐的耐腐蚀釉料的施釉方法，工艺简单，原料易得。本发明制备所得的陶罐釉面具有耐腐蚀性能优异的特点。
Corrosion-resistant glaze for pottery pot and glazing method thereof
一种陶罐的耐腐蚀釉料及其施釉方法
ZHANG MING (Autor:in)
06.08.2021
Patent
Elektronische Ressource
Chinesisch
HEAT-RESISTANT POTTERY AND GLAZE USING BASALT AND MANUFACTURING METHOD THEREOF
| Europäisches Patentamt | 2015
Ceramic glaze with non-cracking glaze surface and glazing method thereof
| Europäisches Patentamt | 2020