The invention discloses an environment-friendly baking-free brick prepared from industrial wastes. The environment-friendly baking-free brick is prepared from the following raw materials in parts by weight: 10 to 20 parts of cement, 20 to 30 parts of sulfate slag, 15 to 20 parts of blast furnace slag, 3 to 5 parts of sepiolite powder, 5 to 10 parts of wollastonite powder, 2 to 5 parts of salt mud, 1 to 3 parts of benzotriazole sodium, 2 to 4 parts of silicic acid modified quaternary ammonium salt-10, 1 to 3 parts of single-ended epoxy polyether modified Meso-tetramethyl-meso-tetra-p-aminophenylcalix[4]pyrrole, 1 to 3 parts of a water reducing agent and 10 to 15 parts of water. The invention further provides a preparation method of the environment-friendly baking-free brick using the industrial waste. The environment-friendly baking-free brick prepared from the industrial waste is higher in pressure resistance, higher in crack resistance, more uniform in performance, better in stability, better in durability and longer in service life.
本发明公开了一种利用工业废弃物的环保免烧砖，其特征在于，是由如下重量份的各原料制成：水泥10‑20份、硫酸渣20‑30份、高炉渣15‑20份、海泡石粉3‑5份、硅灰石粉5‑10份、盐泥2‑5份、苯并三氮唑钠1‑3份、硅酸改性季铵盐‑10 2‑4份、单端环氧基聚醚改性Meso‑四甲基‑meso‑四对氨苯基杯[4]吡咯1‑3份、减水剂1‑3份、水10‑15份。本发明还提供了所述利用工业废弃物的环保免烧砖的制备方法。本发明公开的利用工业废弃物的环保免烧砖耐压程度更高，抗裂强度更大，性能更均一，稳定性更好，耐久性更佳，使用寿命更长。
The invention discloses an environment-friendly baking-free brick prepared from industrial wastes. The environment-friendly baking-free brick is prepared from the following raw materials in parts by weight: 10 to 20 parts of cement, 20 to 30 parts of sulfate slag, 15 to 20 parts of blast furnace slag, 3 to 5 parts of sepiolite powder, 5 to 10 parts of wollastonite powder, 2 to 5 parts of salt mud, 1 to 3 parts of benzotriazole sodium, 2 to 4 parts of silicic acid modified quaternary ammonium salt-10, 1 to 3 parts of single-ended epoxy polyether modified Meso-tetramethyl-meso-tetra-p-aminophenylcalix[4]pyrrole, 1 to 3 parts of a water reducing agent and 10 to 15 parts of water. The invention further provides a preparation method of the environment-friendly baking-free brick using the industrial waste. The environment-friendly baking-free brick prepared from the industrial waste is higher in pressure resistance, higher in crack resistance, more uniform in performance, better in stability, better in durability and longer in service life.
本发明公开了一种利用工业废弃物的环保免烧砖，其特征在于，是由如下重量份的各原料制成：水泥10‑20份、硫酸渣20‑30份、高炉渣15‑20份、海泡石粉3‑5份、硅灰石粉5‑10份、盐泥2‑5份、苯并三氮唑钠1‑3份、硅酸改性季铵盐‑10 2‑4份、单端环氧基聚醚改性Meso‑四甲基‑meso‑四对氨苯基杯[4]吡咯1‑3份、减水剂1‑3份、水10‑15份。本发明还提供了所述利用工业废弃物的环保免烧砖的制备方法。本发明公开的利用工业废弃物的环保免烧砖耐压程度更高，抗裂强度更大，性能更均一，稳定性更好，耐久性更佳，使用寿命更长。
| Europäisches Patentamt | 2024
Preparation process of environment-friendly baking-free brick
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2023
Environment-friendly baking-free brick and preparation process thereof
| Europäisches Patentamt | 2023
Manufacturing method of environment-friendly baking-free light brick
| Europäisches Patentamt | 2021