The embodiment of the invention discloses a bi-component micro cement coating and a preparation process thereof, and is used for solving the technical problems that existing paint surfaces for wall surfaces and floors are easy to crack and damp. According to the embodiment of the invention, the coating is composed of a powder component A and a liquid material component B; the powder component A comprises the components in parts by weight: 200 to 400 parts of ordinary Portland cement, 200 to 400 parts of high-alumina cement, 50 to 100 parts of heavy calcium carbonate, 300 to 350 parts of quartz sand, 50 to 100 parts of quartz powder, 1 to 3 parts of a set retarder, 0.5 to 1 part of fibers, 0.5 to 1 part of first cellulose, 10 to 20 parts of dispersible latex powder, 0.6 to 1 part of a first defoaming agent and 0.5 to 1 part of an early strength agent; and the liquid material component B comprises the components in parts by weight: 300 to 350 parts of modified inorganic silicon resin, 600 to 650 parts of deionized water, 1 to 2 parts of second cellulose, 3 to 5 parts of a surfactant, 0.3 to 0.6 part of a second defoaming agent, 0.1 to 0.2 part of a mildew preventive and 0.5 to 1 part of a dispersing agent.
本发明实施例公开了一种双组分微水泥涂料及其制作工艺，用于解决现有用于墙面以及地面的漆面容易开裂、受潮的技术问题。本发明实施例包括由粉料A组分和液料B组分组成；所述粉料A组分按重量份包括：普硅水泥200‑400份，高铝水泥200‑400份，重钙50‑100份，石英砂300‑350份，石英粉50‑100份，缓凝剂1‑3份，纤维0.5‑1份，第一纤维素0.5‑1份，可分散性乳胶粉10‑20份，第一消泡剂0.6‑1份，早强剂0.5‑1份；所述液料B组分按重量份包括：改性无机硅树脂300‑350份，去离子水600‑650份，第二纤维素1‑2份，表面活性剂3‑5份，第二消泡剂0.3‑0.6份，防霉剂0.1‑0.2份，分散剂0.5‑1份。
The embodiment of the invention discloses a bi-component micro cement coating and a preparation process thereof, and is used for solving the technical problems that existing paint surfaces for wall surfaces and floors are easy to crack and damp. According to the embodiment of the invention, the coating is composed of a powder component A and a liquid material component B; the powder component A comprises the components in parts by weight: 200 to 400 parts of ordinary Portland cement, 200 to 400 parts of high-alumina cement, 50 to 100 parts of heavy calcium carbonate, 300 to 350 parts of quartz sand, 50 to 100 parts of quartz powder, 1 to 3 parts of a set retarder, 0.5 to 1 part of fibers, 0.5 to 1 part of first cellulose, 10 to 20 parts of dispersible latex powder, 0.6 to 1 part of a first defoaming agent and 0.5 to 1 part of an early strength agent; and the liquid material component B comprises the components in parts by weight: 300 to 350 parts of modified inorganic silicon resin, 600 to 650 parts of deionized water, 1 to 2 parts of second cellulose, 3 to 5 parts of a surfactant, 0.3 to 0.6 part of a second defoaming agent, 0.1 to 0.2 part of a mildew preventive and 0.5 to 1 part of a dispersing agent.
本发明实施例公开了一种双组分微水泥涂料及其制作工艺，用于解决现有用于墙面以及地面的漆面容易开裂、受潮的技术问题。本发明实施例包括由粉料A组分和液料B组分组成；所述粉料A组分按重量份包括：普硅水泥200‑400份，高铝水泥200‑400份，重钙50‑100份，石英砂300‑350份，石英粉50‑100份，缓凝剂1‑3份，纤维0.5‑1份，第一纤维素0.5‑1份，可分散性乳胶粉10‑20份，第一消泡剂0.6‑1份，早强剂0.5‑1份；所述液料B组分按重量份包括：改性无机硅树脂300‑350份，去离子水600‑650份，第二纤维素1‑2份，表面活性剂3‑5份，第二消泡剂0.3‑0.6份，防霉剂0.1‑0.2份，分散剂0.5‑1份。
Bi-component micro cement coating and preparation process thereof
一种双组分微水泥涂料及其制作工艺
LIU LIANG (Autor:in)
21.09.2021
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Cement modifier component and preparation method thereof
| Europäisches Patentamt | 2016
Cement wall component and manufacturing process thereof
| Europäisches Patentamt | 2021