Water-added construction quick-drying repair castable and preparation method thereof
The invention belongs to the technical field of refractory materials, and particularly relates to a water-added construction quick-drying repair castable and a preparation method thereof. The water-added construction quick-drying repair castable is prepared from, by weight, 65-75 parts of bauxite particles, 10-20 parts of bauxite fine powder, 5-7 parts of solid phosphoric acid and 6 parts of water. The raw materials are weighed in parts by mass, mixed, and uniformly stirred, vibration construction is conducted after stirring is completed, and sintering is conducted according to a standard heating curve, so that the quick-drying repair castable can be used, and by adding the solid phosphoric acid, all advantages and characteristics of the phosphoric acid combined quick-drying material are reserved, but a matched phosphoric acid solution of the material is removed, and thus the transportation convenience and the customer construction safety are greatly improved. Through water-added contruction, the construction convenience is improved, the excellent performance of the material is reserved, the infiltration resistance and chemical erosion resistance of the material are improved by adding water for construction, and the quick-drying repair castable is excellent in performance, safe in construction and suitable for popularization and application.
本发明属于耐火材料技术领域，尤其涉及一种加水施工的快干型修补浇注料及其制备方法，包括以下重量份数的原料组分制成：铝矾土颗粒65‑75份，铝矾土细粉10‑20份，固体磷酸5‑7份以及6份的水；将各组分原料按质量份数称取混合后搅拌均匀，搅拌完成后振动施工，按照标准升温曲线烧结后即可使用，本发明通过添加固体磷酸的方式，保留了磷酸结合快干料的所有优点特性，但去除材料的配套磷酸溶液，大大提高了运输的便捷性和客户施工的安全性；且通过加水施工的方式，提高了施工的便捷性，保留了材料的优秀性能，并提高了材料的抗浸润和抗化学侵蚀的能力，本发明制备的快干型修补浇注料性能优异且施工安全，适合推广使用。
Water-added construction quick-drying repair castable and preparation method thereof
The invention belongs to the technical field of refractory materials, and particularly relates to a water-added construction quick-drying repair castable and a preparation method thereof. The water-added construction quick-drying repair castable is prepared from, by weight, 65-75 parts of bauxite particles, 10-20 parts of bauxite fine powder, 5-7 parts of solid phosphoric acid and 6 parts of water. The raw materials are weighed in parts by mass, mixed, and uniformly stirred, vibration construction is conducted after stirring is completed, and sintering is conducted according to a standard heating curve, so that the quick-drying repair castable can be used, and by adding the solid phosphoric acid, all advantages and characteristics of the phosphoric acid combined quick-drying material are reserved, but a matched phosphoric acid solution of the material is removed, and thus the transportation convenience and the customer construction safety are greatly improved. Through water-added contruction, the construction convenience is improved, the excellent performance of the material is reserved, the infiltration resistance and chemical erosion resistance of the material are improved by adding water for construction, and the quick-drying repair castable is excellent in performance, safe in construction and suitable for popularization and application.
本发明属于耐火材料技术领域，尤其涉及一种加水施工的快干型修补浇注料及其制备方法，包括以下重量份数的原料组分制成：铝矾土颗粒65‑75份，铝矾土细粉10‑20份，固体磷酸5‑7份以及6份的水；将各组分原料按质量份数称取混合后搅拌均匀，搅拌完成后振动施工，按照标准升温曲线烧结后即可使用，本发明通过添加固体磷酸的方式，保留了磷酸结合快干料的所有优点特性，但去除材料的配套磷酸溶液，大大提高了运输的便捷性和客户施工的安全性；且通过加水施工的方式，提高了施工的便捷性，保留了材料的优秀性能，并提高了材料的抗浸润和抗化学侵蚀的能力，本发明制备的快干型修补浇注料性能优异且施工安全，适合推广使用。
Water-added construction quick-drying repair castable and preparation method thereof
一种加水施工的快干型修补浇注料及其制备方法
XU YING (Autor:in) / GUO RUNLAI (Autor:in) / CHEN MIN (Autor:in) / TANG QI (Autor:in) / CHEN ZHIHONG (Autor:in)
26.10.2021
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
| Europäisches Patentamt | 2022
High-wear-resistance quick-drying refractory castable and preparation method thereof
| Europäisches Patentamt | 2020
Quick-drying iron runner castable as well as preparation method ad use method thereof
| Europäisches Patentamt | 2015
Quick-drying explosion-proof high-strength wear-resistant castable
| Europäisches Patentamt | 2021