The invention provides a porcelain material composition and a preparation method of a porcelain plate, and belongs to the field of porcelain building materials. The porcelain material composition is prepared from the following chemical components in percentage by mass: 65 to 70 percent of SiO2, 17 to 19 percent of Al2O3, 0 to 1.5 percent of Fe2O3, 0 to 0.5 percent of TiO2, 1.0 to 3.0 percent of CaO, 0.7 to 1.5 percent of MgO, 3.0 to 4.0 percent of K2O, 1 to 1.8 percent of Na2O and 3.5 to 5.5 percent of ignition loss IL. The composition is used for firing to prepare the porcelain plate, so that the water absorption rate of the finished porcelain plate can be effectively reduced, the strength of the porcelain plate can be improved, and meanwhile, the influence caused by reduction of the glazing amount can be effectively reduced.
本申请提供一种瓷料组合物及瓷板的制备方法，属于陶瓷建材领域。瓷料组合物的化学成分按质量百分比计包括：65～70％的SiO2、17～19％的Al2O3、0～1.5％的Fe2O3、0～0.5％的TiO2、1.0～3.0％的CaO、0.7～1.5％的MgO、3.0～4.0％的K2O、1～1.8％的Na2O以及3.5～5.5％的烧失IL。采用该瓷料组合物进行烧成处理制备瓷板，能有效降低成品瓷板吸水率并提高瓷板强度，同时能有效降低因施釉量降低带来的影响。
Porcelain material composition and preparation method of porcelain plate
The invention provides a porcelain material composition and a preparation method of a porcelain plate, and belongs to the field of porcelain building materials. The porcelain material composition is prepared from the following chemical components in percentage by mass: 65 to 70 percent of SiO2, 17 to 19 percent of Al2O3, 0 to 1.5 percent of Fe2O3, 0 to 0.5 percent of TiO2, 1.0 to 3.0 percent of CaO, 0.7 to 1.5 percent of MgO, 3.0 to 4.0 percent of K2O, 1 to 1.8 percent of Na2O and 3.5 to 5.5 percent of ignition loss IL. The composition is used for firing to prepare the porcelain plate, so that the water absorption rate of the finished porcelain plate can be effectively reduced, the strength of the porcelain plate can be improved, and meanwhile, the influence caused by reduction of the glazing amount can be effectively reduced.
本申请提供一种瓷料组合物及瓷板的制备方法，属于陶瓷建材领域。瓷料组合物的化学成分按质量百分比计包括：65～70％的SiO2、17～19％的Al2O3、0～1.5％的Fe2O3、0～0.5％的TiO2、1.0～3.0％的CaO、0.7～1.5％的MgO、3.0～4.0％的K2O、1～1.8％的Na2O以及3.5～5.5％的烧失IL。采用该瓷料组合物进行烧成处理制备瓷板，能有效降低成品瓷板吸水率并提高瓷板强度，同时能有效降低因施釉量降低带来的影响。
Porcelain material composition and preparation method of porcelain plate
瓷料组合物及瓷板的制备方法
WANG HUI (Autor:in) / WU LIDAN (Autor:in) / XU JINGLIN (Autor:in)