The invention provides a preparation method of porcelain and the prepared porcelain, and belongs to the technical field of ceramics. Comprising a porcelain green body and a glaze layer arranged on the surface of the porcelain green body, the porcelain green body is prepared from a clay material, and the clay material is prepared from the following raw materials: 10-15 parts of kaolin, 5-10 parts of bentonite, 4-7 parts of feldspar, 20-40 parts of talcum powder, 5-7 parts of nano aluminum oxide and 3-5 parts of clay; a glaze material for forming the glaze layer is prepared from the following raw materials: 5 to 10 parts of fluorine-containing nano silicon-aluminum-titanium-cobalt oxide and 12 to 20 parts of kaolin. After the prepared glaze is sprayed on the surface of a biscuit firing green body, the surface contains rich fluorine-containing groups, so that the prepared surface glaze layer has good hydrophobic and oleophobic performance and has a self-cleaning effect, and the prepared porcelain is wider in application range.
本发明提出了一种瓷器的制备方法及制得的瓷器，属于陶瓷技术领域。包括瓷器坯体及设置于瓷器坯体表面的釉层组成，所述瓷器坯体由陶泥料制备而成，所述陶泥料由以下原料制备而成：高岭土10‑15份、膨润土5‑10份、长石4‑7份、滑石粉20‑40份、纳米氧化铝5‑7份、粘土3‑5份；形成釉层的釉料由以下原料制备而成：含氟纳米硅‑铝‑钛‑钴氧化物5‑10份、高岭土12‑20份。本发明制得的釉料喷涂于素烧坯体表面后，表面含有丰富的含氟基团，从而使得制得的表面釉层具有很好的疏水疏油性能，具有自清洁效果，从而使得制得的瓷器应用面更广。
Porcelain preparation method and prepared porcelain
The invention provides a preparation method of porcelain and the prepared porcelain, and belongs to the technical field of ceramics. Comprising a porcelain green body and a glaze layer arranged on the surface of the porcelain green body, the porcelain green body is prepared from a clay material, and the clay material is prepared from the following raw materials: 10-15 parts of kaolin, 5-10 parts of bentonite, 4-7 parts of feldspar, 20-40 parts of talcum powder, 5-7 parts of nano aluminum oxide and 3-5 parts of clay; a glaze material for forming the glaze layer is prepared from the following raw materials: 5 to 10 parts of fluorine-containing nano silicon-aluminum-titanium-cobalt oxide and 12 to 20 parts of kaolin. After the prepared glaze is sprayed on the surface of a biscuit firing green body, the surface contains rich fluorine-containing groups, so that the prepared surface glaze layer has good hydrophobic and oleophobic performance and has a self-cleaning effect, and the prepared porcelain is wider in application range.
本发明提出了一种瓷器的制备方法及制得的瓷器，属于陶瓷技术领域。包括瓷器坯体及设置于瓷器坯体表面的釉层组成，所述瓷器坯体由陶泥料制备而成，所述陶泥料由以下原料制备而成：高岭土10‑15份、膨润土5‑10份、长石4‑7份、滑石粉20‑40份、纳米氧化铝5‑7份、粘土3‑5份；形成釉层的釉料由以下原料制备而成：含氟纳米硅‑铝‑钛‑钴氧化物5‑10份、高岭土12‑20份。本发明制得的釉料喷涂于素烧坯体表面后，表面含有丰富的含氟基团，从而使得制得的表面釉层具有很好的疏水疏油性能，具有自清洁效果，从而使得制得的瓷器应用面更广。
Porcelain preparation method and prepared porcelain
一种瓷器的制备方法及制得的瓷器
KANG JIHAO (Autor:in) / KANG WANGCAI (Autor:in)
07.03.2023
Patent
Elektronische Ressource
Chinesisch
Colored porcelain prepared from waste porcelain and preparation method of same
| Europäisches Patentamt | 2020
Porcelain clay, and porcelain and preparation method thereof
| Europäisches Patentamt | 2021
Porcelain material composition and preparation method of porcelain plate
| Europäisches Patentamt | 2021
| Europäisches Patentamt | 2020
| Europäisches Patentamt | 2020