The invention relates to the technical field of matt glaze ceramic tile manufacturing, and discloses a production method of a 5G matt glaze ceramic tile. The preparation method comprises the following steps: 1, selecting Teng County stone powder, Guangxi potassium sand, Shaoguan bentonite, second-grade stone powder, calcined bauxite, magnesian mud, high-whiteness aluminum sand, Kelong ball clay, jade kaolin, Xinyi potassium sand, Xinyuan ore mud, Wocheng mixed mud and Xinshangpan water-washed kaolin as a preparation blank material; 2, grinding the blank into blank powder by using a ball mill; and 3, spraying the blank powder by using a spraying machine, wherein the temperature of a spraying agent is 700-800 DEG C. According to the production method of the 5G matte glaze ceramic tile, by adopting an ink-jet printing mode, the glaze surface of the ceramic tile is fine and smooth, the stereoscopic impression is strong, the 5G matte glaze surface in the 5G era of China is realized on the ceramic tile, and the 5G matte glaze ceramic tile has some properties better than those of 5G, can be more widely applied and can be suitable for being used in building places such as interior walls, grounds and exterior walls.
本发明涉及哑光釉瓷砖制作技术领域，且公开了一种5G哑光釉瓷砖的生产方法，包括以下步骤：步骤一，选取藤县石粉、广西钾砂、韶关膨润土、二级石粉、煅烧铝钒土、镁质坭、高白铝砂、科龙球土、玉高岭土、信宜钾砂、新原矿坭、沃城混合坭和新上潘水洗高岭土为制作坯料；步骤二，用球磨机将坯料研磨成坯料粉末；步骤三，用喷雾机对坯料粉末进行喷雾造粉，喷雾剂的温度为700～800℃。该种5G哑光釉瓷砖的生产方法，通过采用喷墨打印的印花方式，使得瓷砖釉面细腻，立体感强，使具有中国5G时代5G哑光釉面实现在瓷砖上，具有5G更交出的一些性能，能得到更广泛的应用，可适用于内墙、地面及外墙等建筑场所使用。
Production method of 5G matte glaze ceramic tile
The invention relates to the technical field of matt glaze ceramic tile manufacturing, and discloses a production method of a 5G matt glaze ceramic tile. The preparation method comprises the following steps: 1, selecting Teng County stone powder, Guangxi potassium sand, Shaoguan bentonite, second-grade stone powder, calcined bauxite, magnesian mud, high-whiteness aluminum sand, Kelong ball clay, jade kaolin, Xinyi potassium sand, Xinyuan ore mud, Wocheng mixed mud and Xinshangpan water-washed kaolin as a preparation blank material; 2, grinding the blank into blank powder by using a ball mill; and 3, spraying the blank powder by using a spraying machine, wherein the temperature of a spraying agent is 700-800 DEG C. According to the production method of the 5G matte glaze ceramic tile, by adopting an ink-jet printing mode, the glaze surface of the ceramic tile is fine and smooth, the stereoscopic impression is strong, the 5G matte glaze surface in the 5G era of China is realized on the ceramic tile, and the 5G matte glaze ceramic tile has some properties better than those of 5G, can be more widely applied and can be suitable for being used in building places such as interior walls, grounds and exterior walls.
本发明涉及哑光釉瓷砖制作技术领域，且公开了一种5G哑光釉瓷砖的生产方法，包括以下步骤：步骤一，选取藤县石粉、广西钾砂、韶关膨润土、二级石粉、煅烧铝钒土、镁质坭、高白铝砂、科龙球土、玉高岭土、信宜钾砂、新原矿坭、沃城混合坭和新上潘水洗高岭土为制作坯料；步骤二，用球磨机将坯料研磨成坯料粉末；步骤三，用喷雾机对坯料粉末进行喷雾造粉，喷雾剂的温度为700～800℃。该种5G哑光釉瓷砖的生产方法，通过采用喷墨打印的印花方式，使得瓷砖釉面细腻，立体感强，使具有中国5G时代5G哑光釉面实现在瓷砖上，具有5G更交出的一些性能，能得到更广泛的应用，可适用于内墙、地面及外墙等建筑场所使用。
Production method of 5G matte glaze ceramic tile
一种5G哑光釉瓷砖的生产方法
ZHANG WANYUN (Autor:in)
24.12.2021
Patent
Elektronische Ressource
Chinesisch
Dry granular glaze, matte ceramic tile and preparation method of dry granular glaze
| Europäisches Patentamt | 2023
| Europäisches Patentamt | 2020
Fine matte dry granular glaze ceramic tile and preparation method thereof
| Europäisches Patentamt | 2023
| Europäisches Patentamt | 2015
| Europäisches Patentamt | 2022