Papermaking white mud aerated concrete and preparation method thereof
The invention discloses papermaking white mud aerated concrete and a preparation method of the papermaking white mud aerated concrete. The best mix proportion of the aerated concrete is that the use amount of concrete materials per cubic meter is as follows: 70kg of cement, 112kg of lime, 21kg of gypsum, 469kg of fly ash, 385kg of water, 209g of aluminum powder and 28kg of papermaking white mud calcined at 1000 DEG C or 1200 DEG C.
本发明公开了一种造纸白泥加气混凝土及其制备方法，通过对造纸白泥加气混凝土力学、微观能的研究分析后发现，加气混凝土最佳配合比为每立方米混凝土材料用量：水泥用量70kg、石灰用量112kg、石膏用量21kg、粉煤灰用量469kg、水用量385kg、铝粉用量209g、1000℃或1200℃煅烧处理后造纸白泥28kg。
Papermaking white mud aerated concrete and preparation method thereof
The invention discloses papermaking white mud aerated concrete and a preparation method of the papermaking white mud aerated concrete. The best mix proportion of the aerated concrete is that the use amount of concrete materials per cubic meter is as follows: 70kg of cement, 112kg of lime, 21kg of gypsum, 469kg of fly ash, 385kg of water, 209g of aluminum powder and 28kg of papermaking white mud calcined at 1000 DEG C or 1200 DEG C.
本发明公开了一种造纸白泥加气混凝土及其制备方法，通过对造纸白泥加气混凝土力学、微观能的研究分析后发现，加气混凝土最佳配合比为每立方米混凝土材料用量：水泥用量70kg、石灰用量112kg、石膏用量21kg、粉煤灰用量469kg、水用量385kg、铝粉用量209g、1000℃或1200℃煅烧处理后造纸白泥28kg。
Papermaking white mud aerated concrete and preparation method thereof
一种造纸白泥加气混凝土及其制备方法
LIU HAO (Autor:in) / YANG LEIMING (Autor:in) / HUANG BINGZHANG (Autor:in) / LIANG XIAOQIAN (Autor:in) / LIN JIANXIONG (Autor:in) / XIONG MEISHENG (Autor:in)
15.04.2022
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
White mud autoclaved aerated concrete and preparation method thereof
| Europäisches Patentamt | 2020
Autoclaved aerated concrete, autoclaved aerated concrete slab and preparation method thereof
| Europäisches Patentamt | 2020
Papermaking white mud lightweight concrete as well as preparation method and application thereof
| Europäisches Patentamt | 2024