Low-temperature cracked glaze ceramic product and manufacturing method thereof
The invention provides a low-temperature cracked glaze ceramic product, which comprises a body material and a glaze material, and the body material comprises the following raw materials: kaolin, quartz, potassium feldspar, cordierite, clay, talc, carbon fiber and ceramic micro powder; the glaze comprises the following raw materials: potassium feldspar, albite, kaolin, dolomite, quartz, borax, frit, ferric sulfate and plant ash, and the frit comprises the following raw materials: aluminum oxide, zinc oxide, copper oxide and heavy calcium carbonate. The manufacturing method of the low-temperature cracked glaze ceramic product comprises the following steps: respectively mixing the body material and the glaze material, adding water, performing wet milling by using a ball mill, and sieving to obtain body material slurry and glaze slurry; preparing a green body from the tire slurry, and biscuit-firing; glazing is conducted; and sintering. The ceramic product prepared by firing at low temperature is short in firing time and low in temperature, so that the energy consumption is low, the yield is high, and the production cost is reduced; meanwhile, glaze cracks are very special, lines are uniform and clear, and the glaze is fully distributed on the surface and is stacked and distributed layer by layer like crystal flowers, so that an antique artistic aesthetic feeling is created.
本发明提供一种低温裂纹釉陶瓷制品，包括胎料和釉料，所述胎料包括以下原料：高岭土、石英、钾长石、堇青石、粘土、滑石、碳纤维、陶瓷微粉；所述釉料包括以下原料：钾长石、钠长石、高岭土、白云石、石英、硼砂、熔块、硫酸铁和草木灰，所述熔块包括以下原料氧化铝、氧化锌、氧化铜、重质碳酸钙。所述低温裂纹釉陶瓷制品的制作方法如下：将胎料和釉料分别混合加水用球磨机湿磨，过筛得到胎料浆和釉浆；胎料浆制作坯体素烧；施釉；烧成。本发明在低温烧制下制得的陶瓷制品，烧制时间短，温度低，从而能耗低，成品率高，降低生产成本；同时釉面龟裂很特别，纹路均匀、清晰，布满器面，像晶花一样层层叠叠分布，营造出一种古香古色的艺术美感。
Low-temperature cracked glaze ceramic product and manufacturing method thereof
The invention provides a low-temperature cracked glaze ceramic product, which comprises a body material and a glaze material, and the body material comprises the following raw materials: kaolin, quartz, potassium feldspar, cordierite, clay, talc, carbon fiber and ceramic micro powder; the glaze comprises the following raw materials: potassium feldspar, albite, kaolin, dolomite, quartz, borax, frit, ferric sulfate and plant ash, and the frit comprises the following raw materials: aluminum oxide, zinc oxide, copper oxide and heavy calcium carbonate. The manufacturing method of the low-temperature cracked glaze ceramic product comprises the following steps: respectively mixing the body material and the glaze material, adding water, performing wet milling by using a ball mill, and sieving to obtain body material slurry and glaze slurry; preparing a green body from the tire slurry, and biscuit-firing; glazing is conducted; and sintering. The ceramic product prepared by firing at low temperature is short in firing time and low in temperature, so that the energy consumption is low, the yield is high, and the production cost is reduced; meanwhile, glaze cracks are very special, lines are uniform and clear, and the glaze is fully distributed on the surface and is stacked and distributed layer by layer like crystal flowers, so that an antique artistic aesthetic feeling is created.
本发明提供一种低温裂纹釉陶瓷制品，包括胎料和釉料，所述胎料包括以下原料：高岭土、石英、钾长石、堇青石、粘土、滑石、碳纤维、陶瓷微粉；所述釉料包括以下原料：钾长石、钠长石、高岭土、白云石、石英、硼砂、熔块、硫酸铁和草木灰，所述熔块包括以下原料氧化铝、氧化锌、氧化铜、重质碳酸钙。所述低温裂纹釉陶瓷制品的制作方法如下：将胎料和釉料分别混合加水用球磨机湿磨，过筛得到胎料浆和釉浆；胎料浆制作坯体素烧；施釉；烧成。本发明在低温烧制下制得的陶瓷制品，烧制时间短，温度低，从而能耗低，成品率高，降低生产成本；同时釉面龟裂很特别，纹路均匀、清晰，布满器面，像晶花一样层层叠叠分布，营造出一种古香古色的艺术美感。
Low-temperature cracked glaze ceramic product and manufacturing method thereof
一种低温裂纹釉陶瓷制品及其制作方法
ZENG XIANCHENG (Autor:in) / WANG JIANGUO (Autor:in)
29.07.2022
Patent
Elektronische Ressource
Chinesisch
Cracked glaze, preparation method thereof and sanitary ceramic containing cracked glaze
| Europäisches Patentamt | 2024
| Europäisches Patentamt | 2024
| Europäisches Patentamt | 2016
Preparation method of 3D printing semi-opaque cracked green glaze ceramic product
| Europäisches Patentamt | 2023