Floating bead high-resistance plate and preparation method thereof
The invention relates to the technical field of floating bead plates, in particular to a floating bead high-resistance plate and a preparation method thereof.The floating bead high-resistance plate is prepared from, by weight, 20-50 parts of floating beads, 10-20 parts of calcium oxide, 80-95 parts of aluminate cement, 6-12 parts of basalt fibers, 1-6 parts of glass beads and 0.1-0.5 part of graphene oxide powder; wherein the particle size of the graphene oxide powder is 30-60 [mu] m, the particle size of the glass beads is 100-250 [mu] m, the diameter of the basalt fiber is 10-20 [mu] m, and the length of the basalt fiber is 6-15 mm. The floating bead high-resistance plate has excellent compression resistance and breaking strength on the basis of low density and excellent fire resistance and heat insulation performance, can be independently applied to smoke prevention and exhaust air pipes, steel structure fire protection, fire-resistant cable tray boxes and the like, and can meet the application requirement for high strength without the help of a metal protection layer.
本发明涉及漂珠板技术领域，具体涉及一种漂珠高耐板及其制备方法，其由以下重量份的成分构成：漂珠20‑50份，氧化钙10‑20份，铝酸盐水泥80‑95份，玄武岩纤维6‑12份，玻璃微珠1‑6份，氧化石墨烯粉末0.1‑0.5份；其中，所述氧化石墨烯粉末的粒度为30‑60μm，所述玻璃微珠的粒度为100‑250μm，所述玄武岩纤维的直径为10‑20μm，长度为6‑15mm。本发明的漂珠高耐板在密度低，耐火和隔热性能优异的基础上，兼具优异的抗压和抗折强度，在防排烟风管、钢结构防火保护、耐火电缆槽盒等的应用上，可实现独立应用，无需借助金属保护层即可满足有高强度要求的应用需求。
Floating bead high-resistance plate and preparation method thereof
The invention relates to the technical field of floating bead plates, in particular to a floating bead high-resistance plate and a preparation method thereof.The floating bead high-resistance plate is prepared from, by weight, 20-50 parts of floating beads, 10-20 parts of calcium oxide, 80-95 parts of aluminate cement, 6-12 parts of basalt fibers, 1-6 parts of glass beads and 0.1-0.5 part of graphene oxide powder; wherein the particle size of the graphene oxide powder is 30-60 [mu] m, the particle size of the glass beads is 100-250 [mu] m, the diameter of the basalt fiber is 10-20 [mu] m, and the length of the basalt fiber is 6-15 mm. The floating bead high-resistance plate has excellent compression resistance and breaking strength on the basis of low density and excellent fire resistance and heat insulation performance, can be independently applied to smoke prevention and exhaust air pipes, steel structure fire protection, fire-resistant cable tray boxes and the like, and can meet the application requirement for high strength without the help of a metal protection layer.
本发明涉及漂珠板技术领域，具体涉及一种漂珠高耐板及其制备方法，其由以下重量份的成分构成：漂珠20‑50份，氧化钙10‑20份，铝酸盐水泥80‑95份，玄武岩纤维6‑12份，玻璃微珠1‑6份，氧化石墨烯粉末0.1‑0.5份；其中，所述氧化石墨烯粉末的粒度为30‑60μm，所述玻璃微珠的粒度为100‑250μm，所述玄武岩纤维的直径为10‑20μm，长度为6‑15mm。本发明的漂珠高耐板在密度低，耐火和隔热性能优异的基础上，兼具优异的抗压和抗折强度，在防排烟风管、钢结构防火保护、耐火电缆槽盒等的应用上，可实现独立应用，无需借助金属保护层即可满足有高强度要求的应用需求。
Floating bead high-resistance plate and preparation method thereof
一种漂珠高耐板及其制备方法
ZHANG AIJUN (Autor:in) / LI WANGANG (Autor:in) / LI YAHUI (Autor:in) / HUANG LIPING (Autor:in) / HE HAIGUANG (Autor:in) / SUN LIN (Autor:in)
25.11.2022
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Rock magnesium floating bead plate and preparation method thereof
| Europäisches Patentamt | 2023
Floating bead silicon crystal heat-insulating refractory plate and preparation process thereof
| Europäisches Patentamt | 2023
HPMC-floating bead composite lightweight high-strength foam concrete and preparation method thereof
| Europäisches Patentamt | 2023
High-wear-resistance zirconium oxide bead and preparation method thereof
| Europäisches Patentamt | 2021
| Europäisches Patentamt | 2023