Airport road rubber gobi aggregate concrete and preparation method thereof
The invention discloses airport road rubber gobi aggregate concrete and a preparation method thereof, and the airport road rubber gobi aggregate concrete comprises 500 parts by mass of cement, 290 parts by mass of water, 1080 parts by mass of gobi coarse aggregate, 495-885 parts by mass of gobi fine aggregate, 45-90 parts by mass of rubber aggregate, 35 parts by mass of silicon powder and a polycarboxylic acid water reducer. The mixing amount of the polycarboxylic acid water reducer is 0.3% of the weight of the cement, the particle size of the gobi coarse aggregate is 20-37.5 mm, the particle size of the gobi coarse aggregate is 0.15-4.75 mm, the rubber aggregate is waste tire crushed particles, and the particle size of the waste tire crushed particles is 1.18-2 mm. The method solves the problems that a large amount of gobi gravel abandoned materials are generated by gobi roadbed filling and digging, and the recycling ways of the gobi gravel are few.
本发明公开了一种机场道路橡胶戈壁集料混凝土及制备方法，包括500质量份的水泥、290质量份的水、1080质量份的戈壁粗集料、495～885质量份的戈壁细集料、45～90质量份的橡胶集料、35质量份的硅粉以及聚羧酸性减水剂，所述聚羧酸性减水剂的掺量为所述水泥重量的0.3％，所述戈壁粗集料的粒径为20～37.5mm，所述戈壁粗集料的粒径为0.15～4.75mm，所述橡胶集料为废旧轮胎粉碎颗粒，所述废旧轮胎粉碎颗粒的粒径为1.18～2mm。本发明解决了戈壁路基填挖产生大量戈壁碎石弃方材料，存在戈壁碎石再生利用途径少的问题。
Airport road rubber gobi aggregate concrete and preparation method thereof
The invention discloses airport road rubber gobi aggregate concrete and a preparation method thereof, and the airport road rubber gobi aggregate concrete comprises 500 parts by mass of cement, 290 parts by mass of water, 1080 parts by mass of gobi coarse aggregate, 495-885 parts by mass of gobi fine aggregate, 45-90 parts by mass of rubber aggregate, 35 parts by mass of silicon powder and a polycarboxylic acid water reducer. The mixing amount of the polycarboxylic acid water reducer is 0.3% of the weight of the cement, the particle size of the gobi coarse aggregate is 20-37.5 mm, the particle size of the gobi coarse aggregate is 0.15-4.75 mm, the rubber aggregate is waste tire crushed particles, and the particle size of the waste tire crushed particles is 1.18-2 mm. The method solves the problems that a large amount of gobi gravel abandoned materials are generated by gobi roadbed filling and digging, and the recycling ways of the gobi gravel are few.
本发明公开了一种机场道路橡胶戈壁集料混凝土及制备方法，包括500质量份的水泥、290质量份的水、1080质量份的戈壁粗集料、495～885质量份的戈壁细集料、45～90质量份的橡胶集料、35质量份的硅粉以及聚羧酸性减水剂，所述聚羧酸性减水剂的掺量为所述水泥重量的0.3％，所述戈壁粗集料的粒径为20～37.5mm，所述戈壁粗集料的粒径为0.15～4.75mm，所述橡胶集料为废旧轮胎粉碎颗粒，所述废旧轮胎粉碎颗粒的粒径为1.18～2mm。本发明解决了戈壁路基填挖产生大量戈壁碎石弃方材料，存在戈壁碎石再生利用途径少的问题。
Airport road rubber gobi aggregate concrete and preparation method thereof
机场道路橡胶戈壁集料混凝土及制备方法
WANG MENG (Autor:in) / CHEN ZONGPING (Autor:in) / YU JIANG (Autor:in) / HUANG YUMING (Autor:in) / MAHATI YEHOFEN (Autor:in) / LIAO HAOYU (Autor:in) / LI CHAO (Autor:in)
07.03.2023
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
Gobi aggregate concrete and preparation method thereof
| Europäisches Patentamt | 2022
Preparation method of modified rubber aggregate and road cement concrete
| Europäisches Patentamt | 2023
Lightweight aggregate geopolymer rubber concrete and preparation method thereof
| Europäisches Patentamt | 2024
High-performance road rubber concrete and preparation method thereof
| Europäisches Patentamt | 2021