Glaze, non-slip brick with dry-grain-imitating effect and preparation method of non-slip brick
The invention discloses a glaze, a non-slip brick with a dry grain imitation effect and a preparation method of the non-slip brick, and the glaze is prepared from the following components in parts by weight: 20-22 parts of potassium feldspar, 16-18 parts of albite, 18-19 parts of quartz, 8-9 parts of barium carbonate, 4-6 parts of zinc oxide, 4-5 parts of calcined kaolin, 3-5 parts of calcined alumina, 8-9 parts of nepheline powder, 9-11 parts of kaolin and 9-15 parts of zirconium silicate. According to the technical scheme, the glaze well combined with the green body is adopted as the glaze of the ground glaze layer, the glaze and the green body are well adhered, and the glaze can be fused with the glaze of the double-peak throwing glaze layer through the firing step, so that the double-peak throwing glaze layer is tightly combined on the ground glaze layer, and the non-slip brick with the dry-grain-imitating effect is good in wear resistance and good in anti-slip effect. And subsequent glaze layers such as an anti-slip glaze layer and a double-peak throwing glaze layer can be fused conveniently in the firing process, and wear resistance is achieved due to tight combination of the anti-slip glaze layer and the double-peak throwing glaze layer.
本发明公开一种釉料、具仿干粒效果防滑砖及其制备方法，其中，釉料配方包括：按重量计，钾长石20～22份，钠长石16～18份，石英18～19份，碳酸钡8～9份，氧化锌4～6份，煅烧高岭土4～5份，煅烧氧化铝3～5份，霞石粉8～9份、高岭土9～11份，硅酸锆9～15份。本发明技术方案通过采用与坯体结合良好的釉料作为底釉层的釉料，釉料与坯体密着良好，并可以通过烧成步骤与双峰甩釉层的釉料熔合，使双峰甩釉层紧密结合在底釉层上，既使具仿干粒效果防滑砖耐磨性能佳，又方便了后续的釉层例如防滑釉层与双峰甩釉层在烧成过程中熔合，并因二者紧密结合而耐磨。
Glaze, non-slip brick with dry-grain-imitating effect and preparation method of non-slip brick
The invention discloses a glaze, a non-slip brick with a dry grain imitation effect and a preparation method of the non-slip brick, and the glaze is prepared from the following components in parts by weight: 20-22 parts of potassium feldspar, 16-18 parts of albite, 18-19 parts of quartz, 8-9 parts of barium carbonate, 4-6 parts of zinc oxide, 4-5 parts of calcined kaolin, 3-5 parts of calcined alumina, 8-9 parts of nepheline powder, 9-11 parts of kaolin and 9-15 parts of zirconium silicate. According to the technical scheme, the glaze well combined with the green body is adopted as the glaze of the ground glaze layer, the glaze and the green body are well adhered, and the glaze can be fused with the glaze of the double-peak throwing glaze layer through the firing step, so that the double-peak throwing glaze layer is tightly combined on the ground glaze layer, and the non-slip brick with the dry-grain-imitating effect is good in wear resistance and good in anti-slip effect. And subsequent glaze layers such as an anti-slip glaze layer and a double-peak throwing glaze layer can be fused conveniently in the firing process, and wear resistance is achieved due to tight combination of the anti-slip glaze layer and the double-peak throwing glaze layer.
本发明公开一种釉料、具仿干粒效果防滑砖及其制备方法，其中，釉料配方包括：按重量计，钾长石20～22份，钠长石16～18份，石英18～19份，碳酸钡8～9份，氧化锌4～6份，煅烧高岭土4～5份，煅烧氧化铝3～5份，霞石粉8～9份、高岭土9～11份，硅酸锆9～15份。本发明技术方案通过采用与坯体结合良好的釉料作为底釉层的釉料，釉料与坯体密着良好，并可以通过烧成步骤与双峰甩釉层的釉料熔合，使双峰甩釉层紧密结合在底釉层上，既使具仿干粒效果防滑砖耐磨性能佳，又方便了后续的釉层例如防滑釉层与双峰甩釉层在烧成过程中熔合，并因二者紧密结合而耐磨。
Glaze, non-slip brick with dry-grain-imitating effect and preparation method of non-slip brick
一种釉料、具仿干粒效果防滑砖及其制备方法
XIE WEI (Autor:in) / YAO ZHENCHENG (Autor:in)
18.07.2023
Patent
Elektronische Ressource
Chinesisch
Non-slip glaze and processing method of non-slip glazed brick
| Europäisches Patentamt | 2021
Brick slip, method of manufacturing a brick slip, and brick slip assembly
| Europäisches Patentamt | 2023
BRICK SLIP, METHOD OF MANUFACTURING A BRICK SLIP, AND BRICK SLIP ASSEMBLY
| Europäisches Patentamt | 2023
Glaze for low-radioactivity archaized brick, brick applying glaze and preparation method
| Europäisches Patentamt | 2023
| Europäisches Patentamt | 2020